ABSTRACT:

BACKGROUND OF THE INVENTION
This invention relates to abrasive grain and specifically to alumina abrasive grain that has been made using a sol-gel process.
In such a process an alpha alumina precursor which is usually boehmite is formed into an aqueous sol, optionally in the presence of a seed material effective to reduce the temperature at which alpha alumina is formed upon heating or modifying agents. The sol is then caused to gel, usually by the addition of acid, and the gel is then dried and fired to form alpha alumina. Prior to firing the dried gel can be crushed to abrasive sized particles since this process is less demanding than after the conversion to alpha has been accomplished. If desired modifying additives such as yttria and rare earth metal oxides can be incorporated into the sol or into the dried gel prior to firing.
Such processes produce abrasive grain with very fine crystal structures and this proves to be a distinct advantage over alumina abrasive grits produced by a fusion process. It appears that, in use, the abrasive grit fractures to split off fine crystals thus exposing a fresh cutting surface. By contrast grits produced by a fusion process are made up of much larger crystals and when such an abrasive grit contacts a workpiece the cutting edges on the grit are gradually worn down and its cutting efficiency diminishes with the polishing process. This less efficient cutting is accompanied by an increase in friction and heat build up that can ultimately damage the surface of the workpiece. The life of the particular grit ends when the pressure is so great that the grit is ripped from the bond altogether. By providing for the removal of microcrystals of alumina from a grit, this polishing problem is much reduced with sol-gel alumina abrasive grits.
However this microfracture renewal process is active only when an abrasive tool comprising the sol-gel alumina abrasive grits is used under moderate to high pressure grinding conditions. When lower pressures are used, these may not be sufficient to induce microfracture and some polishing may be observed. There is therefore a need to develop an abrasive grit that is capable of efficient grinding at moderate to low pressures without excessive loss of grits in the process. The present invention provides such grits which are found to have utility at all grinding pressures but the very highest. The process by which they are made is simple, economic and extremely versatile in that it can be tailored to any set of grinding conditions likely to be encountered.
DESCRIPTION OF THE INVENTION
The present invention provides alumina abrasive grits having a crystal size less than five microns, in which essentially all the alumina is in the alpha form, and in which the density is from 3.6 to 3.9 g/cc and in which the abrasive grits comprise randomly dispersed essentially spherical voids with diameters of from 0.1 to 5 micrometers.
While essentially all the alumina is in the alpha form this does not preclude alumina being present also in a form such as a spinel or a magnetoplumbite structure where it is combined with other elements. This limitation is intended to convey therefore that there is essentially no transition phase alumina present in the grit.
The comparatively low density is achieved by the inclusion within the grits of a plurality of uniformly dispersed microvoids which are understood to means voids that are from 0.1 to 5, and preferably 0.5 to 2, micrometers in diameter randomly dispersed throughout the grit. Such microvoids are largely internal to the grain, (though of course some may appear at the surface), and therefore yield an apparent density for the grit that is typically only 85 to 95% of the theoretical density of alpha alumina, (3.98 g/cc). These microvoids provide a built-in fracture path that allow a grit to fracture under lower applied pressures and thus to regenerate cutting surfaces more readily without at the same time leading to unacceptable grit loss during the grinding.
The microvoids are randomly dispersed throughout the grit and by this is meant that they are not dispersed in any regular pattern but are generally found in relatively equal numbers at all parts of the grits. The microvoids are usually individual, essentially spherical shapes but occasionally two or more microvoids are sufficiently close to one another to become a single microvoid. The presence of such multiple structures is within the understanding of the definition of the present invention.
The microvoids can be incorporated into the grits by the addition to an alumina precursor sol of a material that will become uniformly dispersed within the dried gel formed from the sol but which will leave a void after firing to form alpha alumina abrasive grits.
In a preferred process for the production of alpha alumina abrasive grits comprising microvoids, an aqueous polymeric latex comprising particles of polymer that are from 0.1 to 5 micrometers in diameter is added to a boehmite sol in an amount that is from 0.03 to 0.3% by weight based on the weight of alumina, measured as alpha alumina, present in the sol, and the sol is then processed to produce alpha alumina abrasive grits. As indicated above this process typically comprises initially the gelation of the sol so as to fix the distribution of the various components dispersed therein such as modifiers and seeds to promote conversion to the alpha form. The gel is then dried and optionally further modified by incorporation of further modifiers by impregnation and then fired to produce the alpha alumina abrasive grits.
The firing process causes the latex particles to burn out leaving behind microvoids which may be slightly smaller in size that the original latex particles as a result of sintering during the firing which tends to eliminate interstitial voids within the crystal structure. It is therefore important to terminate sintering when the desired density has been reached.
In principle the microvoids can also be created by the incorporation of hollow spheres such as fly ash particles or even of naturally occurring organisms such as yeast or lycopodium powder. It is however essential that these be within the size range specified above and be readily dispersible in the sol without clumping. Hollow particles of a mineral such as for example fly ash can be used but generally it is difficult to obtain particles with the appropriately fine diameter.
The preferred form of creating the microvoids, as indicated above is through the incorporation of a polymer latex. The polymer can ne fully polymerized or a liquid oligomer provided this oligomer does not lose its particulate identity when mixed with the dispersion of the alpha alumina precursor. Polymers that can be used are generally thermoplastic, (though suitable thermosetting resins can be substituted), and include for example polystyrene, polybutadiene, fluoropolymers, polyvinylchloride and acrylate polymers and copolymers.
It is also possible to incorporate a powder of a material such as a carbonate which would decompose upon heating to give a gas which would create the microvoid in the structure. An example of such a compound is magnesium carbonate which decomposes to yield carbon dioxide at about 350° C., which is above the temperature at which the gel is dried. It is also insoluble in water and disperses readily in an aqueous medium such as a boehmite sol. Upon firing the residual MgO can act as a pinning agent by the formation of a spinel with alumina, which helps to maintain the low crystal dimensions. Other salts, which need not be limited to carbonates but could embrace also organic acid salts and water-insoluble decomposable salts, include nitrates and acetates.
The alpha alumina precursor dispersion can also comprise particles of a material effective to seed the conversion of the intermediate to the alpha form of alumina. Typically this seed will be alpha alumina particles with particulate sizes of from 0.01 to 1.0 micrometer. However other crystalline materials that are isostructural with alpha alumina and have lattice parameter

Affiliated with

Also associated with

Rating

Abrasive grain does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with Abrasive grain, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Abrasive grain will most certainly appreciate the feedback.

Rate now

Comments { 0 }

Profile ID: LFUS-PAI-O-2824965