Alloys or metallic compositions – Gold base – Silver containing
Reexamination Certificate
2001-10-02
2003-06-10
King, Roy (Department: 1742)
Alloys or metallic compositions
Gold base
Silver containing
C148S430000
Reexamination Certificate
active
06576187
ABSTRACT:
The present invention essentially relates to an 18 carat grey gold alloy for jewellery. More specifically, the present invention essentially relates to a novel 18 carat grey gold alloy for jewellery which is without currently known whitening agents which are mainly nickel, palladium and cobalt, characterised in that it consists essentially, in addition to the gold, copper, silver and manganese, according to the following proportions in percentages by weight, of:
gold
75-78
silver
1-10
manganese
7-15
remainder of copper to
100.
This alloy is particularly advantageous for manufacturing jewels, notably by the disposable wax casting technique.
Thus, according to a preferred characteristic of the invention, this novel grey gold alloy is without nickel, without palladium and without cobalt. The alloy according to the invention has the advantage of removing the risk of occurrence of allergy caused by the nickel contained in most grey gold alloys of ordinary quality and of being less costly than the grey gold alloys which contain palladium.
TECHNICAL BACKGROUND
The fashion of grey gold alloys appeared in the years 1910-1920, at the same time as the platinum alloys. Platinum was very expensive and its availability was greatly reduced by its use as a strategic metal for industry. Moreover, the legal titre of platinum alloys is 95% whilst that of gold is 75%, by weight.
It was thus sought to obtain a gold-based precious alloy, but the colour of which would approach that of platinum as much as possible.
The difficulty with 18 carat gold alloys which contain about 75% by weight of gold is that the sole 25% remaining of elements to be added must remove the yellow tint of the gold. Amongst all the elements tested, only two have proved to be extremely efficient, nickel and palladium. Their whitening effect enables them to whiten the alloy without adding other white element. The document CH-A-684 616 can be cited for example, which describes an alloy of this type. In this document, grey gold alloys are described which contain 5.5 to 18% of palladium and 2 to 12% of manganese. The grey gold alloys which contain palladium are more costly due to the high price of this element and have low hardness which renders them sensitive to wear. Furthermore, these alloys do not give satisfaction in the context of the disposable wax casting process which is widely used in jewellery, as results from the article by Ralph H. Atkinson in the
Revue Françise des Bijoutiers
-
Horlogers
, No. 220. February 1959, p. 40-44.
Furthermore, the gold alloys which contain nickel are very difficult to work since they are sensitive to fissuring. Then, the very widespread use of nickel in alloys constituting ornamental pieces which are even worn on the skin has led to an allergic sensitisation to this element. At present, about 10% of women and 2% of men have a reaction to nickel. This state of fact will lead to a progressive interdiction of nickel in objects which are intended to be in continued contact with the skin. The phenomenon of allergy is described for example in the document CH-A-684 616, notably on page 3, lines 21 to 25. The alloys of gold and nickel are known to be hard and their working difficult.
The document CH-A-684 616 is again a good example of a gold alloy which contains palladium in the place of nickel, with manganese, the manganese alone not having a sufficient whitening effect. It is necessary to add another whitening element to it, which is silver in general. If another whitening element such as cobalt is added, the alloy thus becomes slightly magnetic. Before refining, the factory waste go through a first sort with a magnet which must remove all the ferrous particles originating from the wear of the tools. If the alloy is magnetic, the filings of gold alloy will go out of the cycle with the ferrous waste.
The document FR-B-2 764 906 ENGELHARD-CLAL describes a solution of a 18 and 14 carat grey gold alloy for jewellery, without nickel, without palladium and without silver, based on gold, copper and manganese. The melting interval of the alloys described is 920-940° C. in having a colour which is difficult to distinguish from that obtained with a grey gold alloy containing palladium.
Despite the fact that the alloys in accordance with this prior art document, by the same applicant, give satisfaction, the present invention aims, in addition to the objectives indicated hereinafter, to provide novel classes of alloy which have the same qualities but additionally having a castability and an appearance of a cast alloy further improved with respect to alloys without silver, notably from the document FR-B-2,764,906. Furthermore, it is even desirable to provide novel alloys which have at least a melting interval in a temperature range lower than those of the prior alloys of the document FR-B-2,764,906, namely in a temperature interval at the most equal to about 920° C.
OBJECT OF THE INVENTION
Thus, the aim of the present invention is to provide a novel gold alloy which is grey in colour, of 18 carats, and which is essentially without classical whitening element such as nickel, palladium and cobalt.
Another main aim of the present invention is to provide a novel grey gold alloy, in particular of 18 carats, which is without classical whitening element such as nickel, palladium, cobalt, and which has a very good castability as well as an increased hardness leading to a good resistance to abrasion.
Another aim of the invention is to solve the novel technical problems set forth above by providing a solution of a grey gold alloy which eliminates any cause of cutaneous reaction upon continued contact with the skin, and which thus enables its use in jewellery.
Still another aim of the present invention is to solve the novel technical problems set forth above by providing a solution of a grey gold alloy which be capable of being used within the context of the disposable wax casting process, an ancestral process which is advantageously used for manufacturing jewels, an alloy is only useful in this technique when its castability is satisfactory.
DETAILED DESCRIPTION OF THE INVENTION
Within the context of the invention, it has been discovered in a totally unexpected way for the person skilled in the art that the whole of these technical problems set forth was solved by providing a grey gold alloy essentially without classical whitening element such as nickel, palladium and cobalt, characterised in that it consists essentially, in addition to the gold, silver, copper and manganese, according to the following proportions in percentages by weight, of:
gold
75-78
silver
1-10
manganese
7-15
remainder of copper to
100.
According to a preferred embodiment, the amount of manganese for an 18 carat gold alloy is between 7-15, better between 7 and 12% by weight.
According to an advantageous embodiment, the alloy according to the invention can contain 0 to 1%, preferably 0.01 to 1%, by weight of iridium (Ir) and/or of ruthenium (Ru) the presence of which enables the metallurgical structure to be refined.
According to an advantageous mode, the alloy according to the invention can contain 0 to 1%, preferably 0.01 to 1% by weight of silicon (Si) the presence of which enables deoxidising, and increasing the castability.
According to an even more preferred embodiment, a grey gold alloy according to the present invention is selected from the group consisting, in percentages by weight, of:
a) Au75-Ag1-Cu12-Mn12;
b) Au75-Ag3-Cu12-Mn10;
c) Au75-Ag10-Cu8-Mn7;
d) Au75-Ag3-Cu11.9-Mn10-Ir0.1;
e) Au75-Ag3-Cu11.9-Mn10-Ru0.1; and
f) Au75-Ag3-Cu11.5-Mn10-Si0.5.
The grey gold alloy actually further preferred of the present invention is an 18 carat grey gold alloy constituted of Au75-Ag3-Cu12-Mn10. This preferred alloy has a melting interval considered as being the best, namely of between about 900 and 920° C.
According to a second aspect, the present invention also relates to the use of this novel alloy for manufacturing jewels, in particular by the disposable wax casting technique, by virtue of their compatibility, estimated to be perfect
LeMarchand Annie
Ribault Laurent
Cookson Metaux Precieux SA
Dennison, Schultz & Dougherty
King Roy
Wilkins, III Harry D.
LandOfFree
18 carat grey gold alloy, without nickel and without... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with 18 carat grey gold alloy, without nickel and without..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and 18 carat grey gold alloy, without nickel and without... will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-3114108