Synthetic resins or natural rubbers -- part of the class 520 ser – Synthetic resins – Mixing of two or more solid polymers; mixing of solid...
Reexamination Certificate
2002-02-15
2004-08-31
Lipman, Bernard (Department: 1713)
Synthetic resins or natural rubbers -- part of the class 520 ser
Synthetic resins
Mixing of two or more solid polymers; mixing of solid...
C525S124000, C525S127000, C525S129000, C525S130000, C525S326200, C525S327300, C525S329200, C525S328800, C525S330500, C525S374000, C525S375000, C525S380000, C525S384000, C525S386000
Reexamination Certificate
active
06784248
ABSTRACT:
BACKGROUND OF THE INVENTION
1. Field of the Invention
The present invention relates generally to thermosetting compositions that contain copolymers of vinyl monomers. More specifically, the present invention is directed to thermosetting compositions that contain functional copolymers containing isobutylene type monomers.
2. Description of Related Art
Reducing the environmental impact of coating compositions, in particular that associated with emissions into the air of volatile organics during their use, has been an area of ongoing investigation and development in recent years. Accordingly, interest in high solids liquid and powder coatings has been increasing due, in part, to their inherently low volatile organic content (VOC), which significantly reduces air emissions during the application process. While both thermoplastic and thermoset coating compositions are commercially available, thermoset coatings are typically more desirable because of their superior physical properties, e.g., hardness and solvent resistance.
Low VOC coatings are particularly desirable in the automotive original equipment manufacture (OEM) market due to the relatively large volume of coatings that are used. However, in addition to the requirement of low VOC levels, automotive manufacturers have very strict performance requirements of the coatings that are used. For example, automotive OEM clear top coats are typically required to have a combination of good exterior durability, acid etch and water spot resistance, and excellent gloss and appearance. While liquid top coats containing, for example, capped polyisocyanate and polyol components, can provide such properties, they have the undesirable drawback of higher VOC levels relative to higher solids liquid coatings or powder coatings, which have essentially zero VOC levels.
Coating compositions containing polyol and capped polyisocyanate components (“isocyanate cured coatings”) are known and have been developed for use in a number of applications, such as-industrial and automotive OEM topcoats. Such isocyanate cured coating compositions are described in, for example, U.S. Pat. Nos. 4,997,900, 5,439,896, 5,508,337, 5,554,692, and 5,777,061. However, their use has been limited due to deficiencies in, for example, flow, appearance and storage stability. Isocyanate cured coating compositions typically include a crosslinker having two or more capped isocyanate groups, e.g., a trimer of 1-isocyanato-3,3,5-trimethyl-5-isocyanatomethylcyclohexane capped with e-caprolactam, and a hydroxy functional polymer, e.g., an acrylic copolymer prepared in part from a hydroxyalkyl acrylate and/or methacrylate.
Electrodeposition as a coating application method involves deposition of a film-forming composition onto a conductive substrate under the influence of an applied electrical potential. Electrodeposition has become increasingly important in the coatings industry because, by comparison with non-electrophoretic coating means, electrodeposition offers increased paint utilization, improved corrosion protection, and low environmental contamination.
Initially, electrodeposition was conducted with the workpiece being coated serving as the anode. This was familiarly referred to as anionic electrodeposition. However, in 1972, cationic electrodeposition was introduced commercially. Since that time, cationic electrodeposition has steadily gained in popularity and today is by far the most prevalent method of electrodeposition. Throughout the world, more than 80 percent of all motor vehicles produced are given a primer coating by cationic electrodeposition.
Electrodepositable coating compositions comprising active hydrogen-containing polymers which contain onium salt groups are known and have been developed for use, inter alia, in electrodepositable automotive OEM primer coatings. Such electrodepositable coating compositions typically comprise a crosslinking agent having at least two functional groups that are reactive with active hydrogen groups, and an active hydrogen-containing polymer which contains onium salt groups.
Functional polymers used in liquid, powder, and electrodepositable coating compositions are typically random copolymers that include functional group-containing acrylic and/or methacrylic monomers. Such a functional copolymer will contain a mixture of polymer molecules having varying individual functional equivalent weights and polymer chain structures. In such a copolymer, the functional groups are located randomly along the polymer chain. Moreover, the number of functional groups is not divided equally among the polymer molecules, such that some polymer molecules may actually be free of functionality.
In a thermosetting composition, the formation of a three-dimensional crosslinked network is dependent on the functional equivalent weight as well as the architecture of the individual polymer molecules that comprise it. Polymer molecules having little or no reactive functionality (or having functional groups that are unlikely to participate in crosslinking reactions due to their locations along the polymer chain) will contribute little or nothing to the formation of the three-dimensional crosslinked network, resulting in decreased crosslink density and less than optimum physical properties of the finally formed thermoset coating.
Many patents express the potential for using isobutylene-containing polymers in coating compositions. For example, U.S. Pat. No. 6,114,489 to Vicari et al. discloses a coating composition that includes a functional acrylic resin binder; a co-reactant capable of reacting with the functionality of the acrylic binder; a degasser; and a hyperbranched polyester flow and leveling agent. Isobutylene is suggested as a potential co-monomer for use in the acrylic binder as part of a long list of monomers. U.S. Pat. No. 5,552,487 to Clark et al. discloses powder coating compositions that include a copolymer having a reactive functionality and a suitable crosslinking agent capable of reaction with the reactive functionality of the copolymer. The copolymer is a made by copolymerizing functional monomers with other monomers, isobutylene being one among many listed as potential co-monomers. Although only two are referenced herein, of the many patents that express the possibility of using isobutylene-type co-monomers, none actually shows or discloses a working example of such a copolymer.
The fact that no examples of isobutylene-type monomer-containing copolymers in coating compositions can be found is most likely due to the generally non-reactive nature of isobutylene with acrylic and methacrylic monomers. Reactivity ratios for monomers can be calculated using the Alfrey-Price Q-e values (Robert Z. Greenley, Polymer Handbook, Fourth Edition, Brandrup, Immergut and Gulke, editors, Wiley & Sons, New York, N.Y., pp. 309-319 (1999)). The calculations may be carried out using the formulas I and II:
r
1
=(
Q
1
/Q
2
)exp{−
e
1
(
e
1
−e
2
)} I
r
2
=(
Q
2
/Q
1
)exp{−
e
2
(
e
2
−e
1
)} II
where r
1
and r
2
are the respective reactivity ratios of monomers 1 and 2, and Q
1
and Q
2
and e
1
and e
2
are the respective reactivity and polarity values for the respective monomers (Odian,
Principals of Polymerization
, 3
rd
Ed., Wiley-Interscience, New York, N.Y., Chapter 6, pp. 452-467 and 489-491 (1991)). Table 1 shows the calculated reactivity ratios of selected monomers with isobutylene:
TABLE 1
Monomer
r
1
(isobutylene)
r
2
Methyl acrylate
0.10
13.67
Glycidyl methacrylate
0.08
34.17
Methacrylic acid
0.09
39.71
As one skilled in the art of polymer chemistry can appreciate, when r
1
is near zero and r
2
has a value of 10 or more, monomer 2 is reactive toward both monomers and monomer 1 is reactive toward neither monomer. In other words, it is extremely difficult to prepare copolymers having significant amounts of both monomers. It is not surprising then that no examples can be found of coating compositions that include isobutylene-type monomer-containing copolym
Coca Simion
Coleridge Edward R.
McCollum Gregory J.
O'Dwyer James B.
Poole James E.
Lipman Bernard
PPG Industries Ohio Inc.
Uhl William J.
LandOfFree
Thermosetting compositions containing alternating copolymers... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Thermosetting compositions containing alternating copolymers..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Thermosetting compositions containing alternating copolymers... will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-3291657