Synthetic resins or natural rubbers -- part of the class 520 ser – Synthetic resins – Mixing of two or more solid polymers; mixing of solid...
Reexamination Certificate
2002-10-15
2004-12-28
Lipman, Bernard (Department: 1713)
Synthetic resins or natural rubbers -- part of the class 520 ser
Synthetic resins
Mixing of two or more solid polymers; mixing of solid...
C525S328700, C525S386000
Reexamination Certificate
active
06835784
ABSTRACT:
The present invention relates to novel high-molecular-weight crosslinked polyvinyl butyrals, a process for their production, and their use.
It is known that polyvinyl butyrals can be extruded together with plasticizers to give films used in particular in laminated safety glass.
To increase the molecular weight of polyvinyl butyrals of this type, EP-A-0 211 818 proposes crosslinking polyvinyl butyrals via stable intermolecular diacetal links. The crosslinking takes place via aldehydes having at least two aldehyde groups. The crosslinker here is added prior to or during the acetalization of the polyvinyl alcohols with butyraldehyde.
However, due to the high reactivity of the aldehydes, crosslinking of polyvinyl butyrals with dialdehydes gives polyvinyl butyrals which are highly crosslinked and of very high molecular weight, and which are therefore not always soluble. In addition, low selectivity means that the crosslinking reaction is difficult to control, and it is therefore very difficult to produce products of reproducible quality.
The object of the present invention was therefore to provide polyvinyl butyrals whose mechanical strength is higher than non-crosslinked products and which, in addition, can be prepared reproducibly.
Surprisingly, it has been found that high-molecular-weight polyvinyl butyrals can be prepared reproducibly by crosslinking with di- and/or polycarboxylic acids or with esters of these.
The present invention therefore provides high-molecular-weight, crosslinked polyvinyl butyral obtainable by crosslinking a polyvinyl butyral with at least one di- and/or polycarboxylic acid or with derivatives, preferably esters, of these as crosslinking reagent.
Preferred crosslinking agents are oxalic acid, malonic acid, succinic acid, glutaric acid, adipic acid, maleic acid, fumaric acid, itaconic acid, phthalic acid, terephthalic acid, and also esters of these.
Particularly preferred crosslinking reagents are aliphatic diesters of the formula (I)
ROOC—(CH
2
)
n
—COOR (I)
where the radicals R are identical or different and, independently of one another, are C
1
-C
4
-alkyl, and n is from 0 to 4, preferably 0.
Use is made particularly of diethyl and/or dimethyl oxalate.
The crosslinked polyvinyl butyrals therefore have the following structural units:
P—OOC—(CH
2
)
n
—COO—P
where n is from 0 to 4, and P is each of the polyvinyl butyral chains.
The polyvinyl butyrals of the invention have chemical strength markedly higher than that of conventional products.
The starting materials used may be any of the polyvinyl butyrals known to the skilled worker, and there is therefore no restriction of any kind on the molecular weight of the starting polyvinyl butyrals. However, preference is given to polyvinyl butyrals with a molar mass of at least 50 000 g/mol. The polyvinyl alcohol contents of the polyvinyl butyrals used as starting materials are preferably from 10 to 25% by weight, and particularly preferably from 16 to 23% by weight. The polyvinyl acetate contents of the polyvinyl butyrals used as starting materials are preferably from 0 to 20% by weight.
In one preferred embodiment, the high-molecular-weight, crosslinked polyvinyl butyrals prepared according to the invention comprise plasticizer or plasticizer mixtures. The plasticizers used here may be any of the plasticizers known to the skilled worker, in particular esters of polybasic acids, of polyhydric alcohols, or of oligoether glycols. Examples of preferred plasticizers are diesters of aliphatic diols, or of aliphatic polyether diols, or of polyether polyols, with aliphatic carboxylic acids, preferably diesters of polyalkylene oxides, in particular diesters of di-, tri- or tetraethylene glycol with aliphatic C
6
-C
10
carboxylic acids, or else diesters of aliphatic or aromatic C
2
-C
18
dicarboxylic acids with aliphatic C
4
-C
12
alcohols, preferably dihexyl adipate, or else mixtures of the esters mentioned. The amounts of the plasticizer used are the usual amounts known to the skilled worker, and the plasticizer content here is preferably from 25 to 60 parts by weight, based on 100 parts by weight of PVB.
The present invention therefore also provides a process for preparing the polyvinyl butyrals of the invention, which comprises adding the crosslinking reagent, and also, where appropriate, the plasticizer, to the polyvinyl butyral, homogenizing the mixture, where appropriate, and thermally crosslinking the same at temperatures within the range from 80 to 280° C.
In one preferred embodiment, the crosslinking is catalyzed by adding alkaline or acidic additives.
Examples of alkaline or acidic additives which may be used are the hydroxides, alkanoates, carboxylates, sulfates, chlorides, nitrates, or phosphates of alkali metals and/or of alkaline earth metals, and free organic and/or inorganic acids, and amines.
The preparation of the high-molecular-weight, crosslinked polyvinyl butyrals of the invention is described below in greater detail in one preferred embodiment, but without limitation thereto.
The crosslinking reagent may be in dissolved form, for example in the plasticizer, when added to the polyvinyl butyral, and the mixture may then be homogenized.
The concentration of the crosslinking reagent here is preferably in the range from 0.01 to 10% by weight, particularly preferably in the range from 0.1 to 3% by weight, and in particular in the range from 0.1 to 1% by weight, based in each case on polyvinyl butyral.
The thermal crosslinking may be carried out in any of the heatable assemblies known to the skilled worker, e.g. kneaders or autoclaves. However, the crosslinking preferably takes place in an extruder, and indeed preferably at melt temperatures in the range from 80 to 280° C.
The crosslinking reaction is promoted by the polymer alkalinity usually established so as to stabilize the polyvinyl butyral.
The present application also provides a molding composition comprising the high-molecular-weight crosslinked polyvinyl butyral of the invention.
The extrusion process described can also process the polyvinyl butyral of the invention directly to give a film, with the aid of a slot die. Processes for producing polyvinyl butyral films are well known to the skilled worker. Films made from he high-molecular-weight crosslinked polyvinyl butyrals of the invention may also comprise other conventional additives, e.g. oxidation stabilizers, UV stabilizers, dyes, pigments, and also release agents.
The present application therefore also provides a film comprising the high-molecular-weight, crosslinked polyvinyl butyral of the invention.
The films have high tear strength, particularly advantageous for producing laminated safety glass, which is the main application sector for the films.
The present invention therefore also provides the use of the films of the invention for producing laminated safety glass.
The invention is described in detail below using examples, but without being restricted thereby
BRIEF DESCRIPTION OF THE DRAWINGS
Certain preferred embodiments are described below with reference to the accompanying figures in which:
FIG. 1
is a schematic illustration of the orientation of test impacts.
FIG. 2
is a graphical illustration of the results of a standard pummel test.
Test Methods
Polyvinyl Alcohol Content of PVB
For this test, the PVB is acetylated with an excess of acetic anhydride in pyridine. After the reaction, the excess acetic anhydride is hydrolyzed with water and the resultant solution is titrated potentiometrically with sodium hydroxide solution. The PVOH content is calculated from the amount of sodium hydroxide solution consumed.
Polyvinyl Acetate Content of PVB
For this test, the PVB is dissolved in a benzyl alcohol/ethanol mixture. The acetyl groups are saponified with an excess of alcoholic potassium hydroxide. The excess potassium hydroxide solution is back-titrated with hydrochloric acid. The polyvinyl acetate content is calculated from the amount of hydrochloric acid consumed.
Mw, Mn
Molecular weights of the polyvinyl butyrals present in the molding compositions are determined by
Banner & Witcoff LTD
Kuraray Specialties Europe GmbH
Lipman Bernard
LandOfFree
High-molecular, cross-linked polyvinyl butyrals, method for... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with High-molecular, cross-linked polyvinyl butyrals, method for..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and High-molecular, cross-linked polyvinyl butyrals, method for... will most certainly appreciate the feedback.