Synthetic resins or natural rubbers -- part of the class 520 ser – Synthetic resins – Processes of preparing a desired or intentional composition...
Reexamination Certificate
2001-07-24
2004-05-11
Yoon, Tae H. (Department: 1714)
Synthetic resins or natural rubbers -- part of the class 520 ser
Synthetic resins
Processes of preparing a desired or intentional composition...
C524S442000, C524S443000, C524S493000, C524S791000
Reexamination Certificate
active
06734229
ABSTRACT:
FIELD OF THE INVENTION
The present invention is directed to a composite material having high mechanical strength, increased glass transition temperature and high optical clarity or transparency, and to a process for producing the same. The composite material comprises a polymer with polar or polarizable groups, a layered silicate dispersed therein, and a substance such as a surfactant which controls the crystalline structure or molecular conformation of the polymer.
BACKGROUND OF THE INVENTION
Glass and mineral reinforced polymers have been produced to increase the strength and barrier properties of many polymer applications. Recently, polymer silicate composites have been produced to attain the same degree of stiffness and strength with less ceramic content than comparable glass or mineral reinforced polymers. These materials take the form of polymer-ceramic nanocomposites with layered silicates as the inorganic phase. The materials design and synthesis rely on the ability of layered silicates to intercalate in the galleries between their layers a wide range of monomers and polymers.
Polymer layered silicate composites exhibit desirable properties for use in many commercial applications. These composites are stiffer and stronger and have better barrier properties than comparable glass or mineral reinforced polymers with less inorganic content, making them lighter in weight. Additionally, these silicate polymer composites have increased thermal stability and self-extinguishing properties. Composites with these characteristics have applications in paint, varnishes, lacquers, liquid resins, epoxies and the like.
Because the silicate-layered composites achieve composite properties at much lower volume fraction of reinforcement, they avoid many of the costly and cumbersome fabrication techniques common to conventional fiber or mineral reinforced polymers. Known methods of making silicate-polymer composites involve forming the polymer in situ or carrying out intercalation by melting. U.S. Pat. No. 4,455,382 to Wu teaches the production of a polar liquid to disintegrate a glass-ceramic body prior to reaction with organic polycations to form the interlayer of the crystals to form an organic-inorganic composite. U.S. Pat. No. 4,739,007 to Okada et al teaches the use of an aqueous swelling agent mixed with a crushed clay material followed by ion exchange with an organic cation previously mixed with the swelling agent to produce a composite material. U.S. Pat. No. 4,894,411 to Okada et al expands on this method by introducing a polyamide monomer as the organic cation followed by polymerization of the monomer by heating in the presence of a phenol or polyamine stabilizer. U.S. Pat. No. 4,810,734 to Kawasumi et al teaches mixing a layered clay with a swelling agent to form a complex that is mixed with a monomer to intercalate into the layered material followed by polymerization of the monomer to form a composite material. U.S. Pat. No. 5,955,535 to Vaia et al teaches the intercalation of a polymer into the galleries of layered silicate by heating the polymer-silicate mixture to above the melting or glass transition temperature of the polymer in the absence of a solvent. This last method produces the sought after polymer-clay composites with small visible flecks of the organically modified clay and other suspended impurity materials thereby limiting their potential use in applications requiring transparency and temperature resistance. Accordingly, a new method of producing polymer-clay composites resulting in a transparent composite with better thermal properties is desired.
SUMMARY OF THE INVENTION
The process of the present invention produces composite polymer clay materials in a process using a solvent to intercalate the polymer in the clay material without in situ formation of the polymer or melting of the polymer. This process provides less expensive synthetic pathways to produce composite polymer clay materials with enhanced strength and stiffness.
The process utilizes a solvent for fabricating modified polymer clay materials in a process that is cleaner than a melt fabrication process and therefore likely to result in a transparent final material. In this process, an aliphatic salt is introduced into the galleries of a layered silicate in the presence of a solvent. The polymer is then mixed with the silicate in the same or another appropriate solvent and the solvent is evaporated, resulting in an optically transparent modified clay with an intercalated polymer.
REFERENCES:
patent: 4455382 (1984-06-01), Wu
patent: 4739007 (1988-04-01), Okada et al.
patent: 4810734 (1989-03-01), Kawasumi et al.
patent: 4894411 (1990-01-01), Okada et al.
patent: 5032546 (1991-07-01), Giannelis et al.
patent: 5032547 (1991-07-01), Giannelis et al.
patent: 5698624 (1997-12-01), Beall et al.
patent: 5849830 (1998-12-01), Tsipursky et al.
patent: 5955535 (1999-09-01), Vaia et al.
Barrow;Physical Chemistry; The kinetic-molecular theory of gases, Chapter 2, pp. 50-51; and Liquids, Chapter 16, pp. 528-529.
Chen, An X-Ray and Chemical Study of Iron in Smectite Clays, A dissertation to the Office of Graduate Education and Research—South Dakota School of Mines and Technology, 1996 pp. 8 and 31-38.
Fuuerstenau et al., “Chemistry of Flotation”, published bySociety of Mining Engineers, 1985, pp. 1 and 92-93.
Giannelis, “Polymer Layered Silicate Nanocomposites”,Adv. Matter, 8:1, 1996 p. 2935.
Gruenwald, “Plastics: How Structure Determines Properties”, Thermal Properties of Polymeric Materials, Chapter 8, pp. 208-209.
Hunter, “Foundations of Colloid Science”, vol. 1, University of Sydney-Australia, pp. 2-3 and 30-31.
Ives (editor), “The Science Basis of Flotation”, Series E: Applied Sciences—No. 75, 1984, pp. 36-37.
Krishnamoorti et al., “Structure and Dynamics of Polymer-Layered Silicate Nanocomposites”,Chem. Mater., 1996, vol. 8, pp. 1728-1734.
Levy et al., “Interlayer Adsorption of Polyvinylpyrrolidone on Montmorillonite”,Journal of Colloid and Interface Science, vol. 50, No. 3, Mar. 1975, pp. 442-450.
Mottana et al., “Guide to Rocks and Minerals”, published by Simon & Schuster Inc., pp. 234-235.
Perloff, et al., Soil Mechanics Principles and Applications, published by The Ronald Press Company, pp. 398-399.
Petrucci, “General Chemistry and Modern Applications”, California State University, Macmillan Publishing Company, pp. 352-355.
Seymour et al., “Polymer Chemistry—An Introduction”, Undergraduate Chemistry A Series of Textbooks, Edited by J.J. Lagowski Department of Chemistry at the University of Texas at Austin, pp. 20-27.
Theng, “The Chemistry of Clay—Organic Reactions”, Published by John Wiley & Sons, pp. 92-93, 208-209 and 268-269.
B.K.G. Theng, “Formation and Properties of Clay-Polymer Complexes”, Soil Bureau, Department of Scientific and Industrial Research, Lower Hutt, New Zealand, Elsevier Scientific Publishing Company, pp. 63-133.
Fairbridge, “The Encyclopedia of Sedimentology”,Encyclopedia of Earth Sciences, vol. VI, pp. 58-61.
The New Encyclopedia Britannica, vol. 21, 15thEdition, pp. 322-323.
Vaia, “Polymer Melt Intercalation in Mica-Type Layered Silicates”, A Dissertation Presented to the Faculty of the Graduate School of Cornell University, May 1995.
LandOfFree
Composite polymer clay material and process for producing... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Composite polymer clay material and process for producing..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Composite polymer clay material and process for producing... will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-3250569