Plastic and nonmetallic article shaping or treating: processes – With measuring – testing – or inspecting – Controlling heat transfer with molding material
Reexamination Certificate
2001-10-10
2004-05-25
Colaianni, Michael (Department: 1734)
Plastic and nonmetallic article shaping or treating: processes
With measuring, testing, or inspecting
Controlling heat transfer with molding material
C264S234000, C264S236000, C264S336000
Reexamination Certificate
active
06740269
ABSTRACT:
BACKGROUND OF THE INVENTION
1. Field of the Invention
The present invention relates to a method and apparatus for treating a disc plate. More specifically, the present invention relates to the method and the apparatus for reducing a warp of an optical disc such as a digital video disc (hereinafter referred to as “DVD”) and a compact disc. Especially, the warp is the one that is caused to a disc plate (of the optical disc) which has been molded through an injection molding. With the thus reduced warp, the disc plate is flattened.
2. Description of the Related Art
Generally, an optical disc plate such as a DVD plate and a compact disc plate is molded through an injection molding.
As is seen in FIG.
14
(A), FIG.
14
(B) and FIG.
14
(C), there is provided a method of molding a disc plate
1
. A resin material is injected into a pair of a first metal mold
10
and a second metal mold
11
for an injection molding. After the injection molding, the resin material is molded into a mold disc plate
1
′ which is to be solidified to become the disc plate
1
. At this point in time, a predetermined information is recorded on one of two surfaces of the mold disc plate
1
′. After this, as is seen in FIG.
14
(B), the first metal mold
10
and the second metal mold
11
are separated from each other (opened). Then, a takeout arm
12
of a takeout mechanism (not shown) moves forward into an area between the first metal mold
10
and the second metal mold
11
, to thereby securely absorb the mold disc plate
1
′ which is high in temperature and is still soft. After this, the takeout arm
12
moves backward, to thereby take the mold disc plate
1
′ out of the first metal mold
10
and the second metal mold
11
.
Then, as is seen in FIG.
14
(C), in a predetermined position, the thus taken out mold disc plate
1
′ is fixedly absorbed directly with a conveyer arm
13
of a conveyance mechanism. The conveyer arm
13
conveys the mold disc plate
1
′ to a cooling stage
14
(next operation).
More specifically, the mold disc plate
1
′ has a first surface and a second surface opposite to the first surface. On the first surface, the mold disc plate
1
′ is fixedly absorbed to a tip end
12
A of the takeout arm
12
. On the second surface, the mold disc plate
1
′ is fixedly absorbed to a tip end
13
A of the conveyer arm
13
. Simultaneously with the absorption of the mold disc plate
1
′ to the tip end
13
A, the tip end
12
A releases (namely, stops absorbing) the mold disc plate
1
′. Then, the conveyer arm
13
turns by substantially 180° with the mold disc plate
1
′ fixedly absorbed to the tip end
13
A. Thereafter, the conveyer arm
13
conveys the mold disc plate
1
′ to the cooling stage
14
. The mold disc plate
1
′ is cooled with the cooling stage
14
, to thereby solidify the resin material of the mold disc plate
1
′. After the solidification, the mold disc plate
1
′ is referred to as the disc plate
1
. The solidification temperature for solidifying the resin material is, for instance, about 90° C.
As described above, the mold disc plate
1
′ soon after being taken out of the first metal mold
10
and the second metal mold
11
is high in temperature, and is sufficiently soft. Therefore, during the sequential operations of i) cooling, ii) solidification of resin material, and iii) becoming the disc plate
1
, the mold disc plate
1
′ causes a considerable deformation such as warp. Conventionally, various methods are taken so as to reduce the warp by adjusting conditions of the injection mold as below:
i) Adjust temperature of the first metal mold
10
and the second metal mold
11
of a mold machine.
ii) Set up temperature difference between the first metal mold
10
and the second metal mold
11
.
iii) Adjust pressure for injecting the resin material.
Even if the warp of the mold disc plate
1
′ is small and reduced through the conventional methods as described above, the mold disc plate
1
′ causes the warp during the time the mold disc plate
1
′ is taken out of the first metal mold
10
and the second metal mold
11
, and during the time the mold disc plate
1
′ is conveyed to the cooling stage
14
. The thus caused warp is attributable to the following repeated description, that is, “The mold disc plate
1
′ soon after being taken out of the first metal mold
10
and the second metal mold
11
of the mold machine is high in temperature and is sufficiently soft.” Moreover, the thus caused warp grows during the cooling operation.
The warp is more specifically described in FIG.
15
(A), FIG.
15
(B) and FIG.
15
(C). The mold disc plate
1
′ is taken out of the first metal mold
10
and the second metal mold
11
of the mold machine. As is seen in FIG.
15
(A), the mold disc plate
1
′ is fixedly absorbed to the tip end
12
A of the takeout arm
12
. Moreover (otherwise), the mold disc plate
1
′ is fixedly absorbed to the tip end
13
A of the conveyer arm
13
. The mold disc plate
1
′ is high in temperature and is sufficiently soft. Therefore, the mold disc plate
1
′ causes the warp when the mold disc plate
1
′ is absorbed substantially in the center area of the mold disc plate
1
′, in such a manner that the warp is bent opposite {(rightward in FIG.
15
(A)} to an absorption side. Especially, the DVD having a thickness of about 0.6 mm (thin) shows the warp (bend) more outstanding than the compact disc having a thickness of about 1.2 mm. Moreover, as is seen in FIG.
15
(B), the mold disc plate
1
′ is turned by the takeout arm
12
at a comparatively high speed with the mold disc plate
1
′ absorbed by the takeout arm
12
, and the mold disc plate
1
′ is conveyed by the conveyer arm
13
at a comparatively high speed with the mold disc plate
1
′ absorbed by the conveyer arm
13
. The above turn and conveyance of the mold disc plate
1
′ causes a wind pressure, to thereby warp the mold disc plate
1
′. Moreover, as is seen in FIG.
15
(C), the mold disc plate
1
′ is cooled on a disc bench
15
of the cooling stage
14
. The mold disc plate
1
′ has such a dead weight as to, as the case may be, cause the warp during a cooling time on the disc bench
15
. Still furthermore, some other cooling stages having different constitution cause a partial deformation of the mold disc plate
1
′ during the cooling time.
The above warp is caused around a center hole (not shown) of the mold disc plate
1
′ radially outward, to thereby form substantially a point symmetry. Some other warps run in such a manner as to form a bilateral symmetry (rightward and leftward) with respect to one to three line(s) through the center hole. The above warps become more obvious as production cycle time of the disc plate
1
is shortened, to thereby encourage the warp (more complicated and larger) of the disc plate
1
.
BRIEF SUMMARY OF THE INVENTION
It is an object of the present invention to provide a method and an apparatus for treating a disc plate.
More specifically, it is the object of the present invention to obtain the disc plate having a warp or a deformation within an allowable limit (tolerance), or to obtain the disc plate which is substantially free from the warp or the deformation. For obtaining the above disc plate, a mold disc plate is spun, during the time the resin material of the mold disc plate is soft (in other words, before solidification of the resin material), at such a high speed as to cause a centrifugal force. Simultaneously with this, the mold disc plate is cooled down. The centrifugal force helps reduce the warp and the deformation.
According to a first aspect of the present invention, there is provided a method of treating a disc plate. The method comprises the following operations of: molding a mold disc plate through an injection molding; and spinning the mold disc plate at a high spin speed. The spinning operation comprises at le
Kobayashi Hideo
Nakamura Masahiro
Shinohara Shinichi
Suzuki Takayuki
Colaianni Michael
Origin Electric Company Limited
Tadesse Yewebdar
LandOfFree
Method and apparatus of treating a disc plate does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Method and apparatus of treating a disc plate, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Method and apparatus of treating a disc plate will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-3208834