Process for producing polycarbonate

Details Process for producing polycarbonate Process for producing polycarbonate

1998-06-06

2004-05-25

Boykin, Terressa (Department: 1711)

Synthetic resins or natural rubbers -- part of the class 520 ser

Synthetic resins

From phenol, phenol ether, or inorganic phenolate

C526S064000, C526S067000, C528S198000

Reexamination Certificate

active

06740729

ABSTRACT:

FIELD OF THE INVENTION
The present invention relates to a process for preparing a polycarbonate from a dialkyl oxalate and a phenolic compound.
BACKGROUND OF THE INVENTION
A process for preparing a polycarbonate from a dialkyl oxalate and a phenolic compound which comprises a first step of transesterifying the starting compound to produce a diaryl oxalate, a second step of decarbonylating the resulting diaryl oxalate to produce a diaryl carbonate, and a third step of subjecting the diaryl carbonate to condensation-polymerization reaction with a polyvalent hydroxyl compound to produce a polycarbonate is described in Japanese Patent Provisional Publication No. 10-152552. The Publication 10-152552 further describes such procedure that a phenolic by-product produced in the condensation-polymerization reaction is recovered and recycled to employ as the phenolic compound in the first step.
In the above-mentioned process, the diaryl carbonate of a high purity can be produced using no troublesome phosgene. Therefore, the diaryl carbonate produced from a dialkyl oxalate and a phenolic compound is favorably employed to react with a polyvalent hydroxyl compound to give a polycarbonate having high quality such as high transparency through condensation-polymerization reaction.
It is also known that a catalyst containing tetramethylammonium hydroxide, tetrabutylammnium hydroxide, or tributylamine is employed as a catalyst for performing a condensation-polymerization reaction for the preparation of a polycarbonate from a diaryl carbonate such as diphenyl carbonate and a polyvalent hydroxyl compound such as bisphenol A.
It has been discovered that a portion of the above-mentioned condensation-polymerization catalyst decomposes at an elevated temperature to produce an amine compound (by-product) such as trimethylamine or tributylamine. The amine by-product is migrated into the recovered phenolic by-product.
According to the further study of the investors, in the case that the phenolic by-product is employed as the phenolic compound in the preparation of the diaryl oxalate, the amine by-product in the phenolic by-product gives adverse effects (e.g., deactivation of the catalyst employed) to the reactions in the steps of transesterification and decarbonylation if the amount of the amine by-product in the phenolic by-product increases.
It has been further discovered that the phenolic by-product recovered in the condensation polymerization reaction is sometimes contaminated with an ethereal real by-product. The ethereal by-product in the phenolic by-product sometimes gives such disadvantageous effects as to disturb recovery of reactants and/or reaction product from the reaction system, if the amount of the ethereal by-product in the phenolic by-product increases.
SUMMARY OF THE INVENTION
The present invention resides in a process for preparing paring polycarbonate which comprises the steps of:
subjecting a dialkyl oxalate and a phenolic compound to transesterification to give a diaryl oxalate;
subjecting the diaryl oxalate to decarbonylation to give a diaryl carbonate;
reacting the diaryl carbonate with a polyvalent hydroxyl compound in the presence of a catalyst containing an amine compound or an ammonium compound to give the polycarbonate, removing a mixture containing a phenolic by-product and an amine by-product;
collecting the mixture;
purifying the mixture so that the amount of the amine by-product in the mixture is reduced to give a phenolic by-product mixture not containing the amine by-product in an amount of more than 600 ppm; and
utilizing thus purified phenolic by-product mixture as a whole fir a part of the phenolic compound give the first step.
In the above-mentioned process, if the collected mixture further contains an ethereal by-product, the mixture is preferably purified to reduce its ethereal by-product content to a level of not more than 600 ppm.
The invention further resides in a process for preparing polycarbonate which comprises the steps of:
subjecting a dialkyl oxalate and a phenolic by-product mixture not containing an amine by-product in an amount of more than 600 ppm to transesterification to give a diaryl oxalate, said phenolic by-product mixture having beer obtained by purifying a mixture containing a phenolic by-product and an amine by-product which was collected in a condensation polymerization reaction for preparing polycarbonate from a dialkyl oxalate and a phenolic compound;
subjecting the diaryl oxalate to decarbonylation to give a diaryl carbonate; and
reacting the diaryl carbonate with a polyvalent hydroxyl compound in the presence of a catalyst containing an amine compound or an ammonium compound to give the polycarbonate.
In the above-mentioned process, if the phenolic by-product mixture further contains an ethereal by-product, the mixture is preferably purified in advance to reduce its ethereal by-product content to a level of not more than 600 ppm.
BRIEF DESCRIPTION OF THE DRAWING
FIGURE is a schematic flow chart to show a process for preparing a polycarbonate according to the present invention.


REFERENCES:
patent: 0832910 (1997-09-01), None

Affiliated with

Also associated with

Rating

Process for producing polycarbonate does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with Process for producing polycarbonate, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Process for producing polycarbonate will most certainly appreciate the feedback.

Rate now

Comments { 0 }

Profile ID: LFUS-PAI-O-3189704