Ethylene polymers

Details Ethylene polymers Ethylene polymers

2001-05-14

2003-02-11

Wu, David W. (Department: 1713)

Synthetic resins or natural rubbers -- part of the class 520 ser

Synthetic resins

Polymers from only ethylenic monomers or processes of...

C526S348000, C526S352000

Reexamination Certificate

active

06518376

ABSTRACT:

FIELD OF THE INVENTION
This invention is related to the field of processes that produce polymers that comprise ethylene.
BACKGROUND OF THE INVENTION
There are many production processes that produce polymers that comprise ethylene. There are also many manufacturing processes that use these polymers to produce useful items. One of these manufacturing processes is called blow molding. In general, blow molding is useful for producing hollow plastic products. A principle advantage of blow molding is its ability to produce hollow shapes without having to join two or more separately molded parts.
1
In order to produce a good quality blow molded product, one needs to start with a good quality polymer. However, producing such good quality polymers is difficult. Therefore, the inventors provide this invention so that such good quality polymers are more readily obtainable.
1
See SPI Plastic Engineering Handbook, Fifth Edition, pages 341-382, edited by M. L. Berins, published by Van Nostrand Reinhold (1991)
SUMMARY OF THE INVENTION
It is an object of this invention to provide a process to polymerize ethylene with at least one olefin to produce a polymer.
It is also an object of this invention to provide a polymer.
In accordance with this invention a process is provided. This process comprises polymerizing ethylene with at least one olefin to produce a polymer, wherein said polymerizing is conducted in a polymerization zone, where said polymerization zone is essentially free of cocatalyst, and wherein said polymerizing is conducted using a catalyst, where said catalyst comprises chromium oxide on a support, and where said support comprises silica, and where said support is essentially free of titania, alumina, and phosphates, and where said catalyst has been activated, and where said catalyst after being activated is then reduced, and wherein said polymerizing is conducted in the presence of hydrogen, and wherein the majority of said olefin is produced by said catalyst, during said polymerizing.
In accordance with this invention, an embodiment is directed to a polymer comprising the following properties: a density from 0.94 to 0.96, a melt index from 0.01 to 0.1 g/10 min., a high load melt index from 5 to 100 g/10 min., and a heterogeneity index from 4 to 14, a shear ratio from 50 to 200, and a Bottle ESCR 33 percent higher than a comparison resin.
DETAILED DESCRIPTION OF THE INVENTION
This invention, in general, is a process comprising polymerizing ethylene with at least one olefin to produce a polymer.
This polymerizing is conducted in a polymerization zone. This polymerization zone can be any convenient reactor. However, currently, it is preferred when the polymerization zone is a loop reactor. It is even more preferred when said polymerizing is conducted in a loop reactor under slurry polymerization conditions. Currently, the preferred diluent for slurry polymerization is isobutane. One of the important aspects of this polymerization zone is that it is essentially free of cocatalysts. This is because cocatalysts adversely affect the formation of the desired product. Examples of such cocatalysts are trihydrocarbylboron compositions and trihydrocarbylaluminum compositions. In general, the amount of these cocatalysts should be less than 1 part per million based on the weight of the diluent. However, it is most preferred when no cocatalyst is added to the polymerization zone.
The catalyst used in this invention comprises chromium oxide on a support. The amount of chromium on said support is in the range of about 0.01 to about 5 weight percent, preferably about 0.1 to about 3 weight percent, and most preferably from 0.5 to 2 weight percent, where such weight percents are based on the weight of the support. The catalyst should be essentially free of chromium halide compounds and organo-chromium compounds (hereafter “HO compounds”) as these HO compounds can adversely affect the formation of the desired polymer. In general, the amount of these HO compounds should be less than 0.2 weight percent based on the weight of the support. However, it is most preferred if no HO compounds were added to the catalyst or to the polymerization zone.
The support comprises silica. Additionally, such support has silica as its major component by weight. It is most preferred when said support consists of silica, with little, if any, impurities. The support should be essentially free of titania, alumina, and phosphates (hereafter “TAP compounds”) since these TAP compounds can adversely affect the formation of the desired product. In general, the amount of these TAP compounds should be less than 0.2 weight percent based on the weight of the support. However, it is most preferred when no TAP compounds are added to the catalyst or to the polymerization zone.
The support should have a surface area from about 200 to about 550 square meters per gram. It is more preferred when the support has a surface area from about 225 to 425 square meters per gram, and it is most preferred when said support has a surface area from 250 to 400 square meters per gram. Surface areas below about 200 m
2
/g have less activity, while surface areas above about 550 m
2
/g produces polymers that have a die swell that is too high, an amount of long chain branching that is too low, and possibly, a melt index that is too low.
The support should have a pore volume from about 0.7 to about 2.5 cubic centimeters per gram. It is more preferred when the support has a pore volume from about 0.8 to about 1.8 cm
3
/g, and it is most when said support has a pore volume from 1 to 1.7 cm
3
/gram. Pore volumes below about 0.7 cm
3
/g have less activity, while pore volumes above about 2.5 cm
3
/g adversely affect the formation of the desired polymer.
Methods of producing these types of catalysts are known in the art. See for example, U.S. Pat. Nos. 3,900,457; 4,081,407; 4,392,990; 4,405,501; 4,735,931; 4,981,831; the disclosures of which are hereby incorporated by reference.
The catalyst should be activated in an oxidizing ambient at a temperature from about 600 to about 900° C. It is even more preferred when the temperature is from about 625 to about 850° C., and it is most preferred when the temperature is from 645 to 820° C. At temperatures below about 600° C. the activity of the catalyst is reduced and the physical properties of the polymer are adversely affected. At temperatures above about 900° C. the catalyst can begin to sinter, thus hurting the polymerizing properties of said catalyst. Currently, the preferred oxidizing ambient is air. This activation is carried out for a time period of about 1 minute to about 50 hours. This allows a portion of the chromium in a lower valance state to be converted to a hexavalent state.
After activation, the catalyst is then reduced in an reducing ambient at a temperature from about 200 to about 550° C. It is even more preferred when the temperature is from about 225 to about 525° C. and it is most preferred when the temperature is from 250 to 500° C. At temperatures below about 200° C. the catalyst may not be sufficiently reduced. At temperatures above about 550° C. the activity of the catalyst can be adversely affected and the melt index of the polymer can be too low. Currently, preferred reducing ambients are a mixture of carbon monoxide and nitrogen, or just carbon monoxide. This reduction is carried out for a time period of about 1 minute to about 50 hours. This allows a portion of the hexavalent chromium to be converted to a lower valent state.
In general, the oxidizing ambient promotes the formation of hexavalent chromium while the reducing ambient promotes the formation of chromium atoms that have a valance less than 6.
Said polymerizing is conducted at a temperature from about 94 to about 112° C. However, it is preferred when said polymerizing is conducted at a temperature from about 96 to about 110° C. and it even more preferred when said polymerizing is conducted at a temperature from 98 to 108° C. At temperatures below about 94° C. the activity of the catalyst is adversely affected. At temperatures abo

Affiliated with

Also associated with

Rating

Ethylene polymers does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with Ethylene polymers, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Ethylene polymers will most certainly appreciate the feedback.

Rate now

Comments { 0 }

Profile ID: LFUS-PAI-O-3175051