Radiation imagery chemistry: process – composition – or product th – Electric or magnetic imagery – e.g. – xerography,... – Radiation-sensitive composition or product
Reexamination Certificate
2001-03-07
2002-10-08
Goodrow, John (Department: 1756)
Radiation imagery chemistry: process, composition, or product th
Electric or magnetic imagery, e.g., xerography,...
Radiation-sensitive composition or product
C430S066000, C430S097000, C430S110300, C430S125320
Reexamination Certificate
active
06461780
ABSTRACT:
FIELD OF THE INVENTION
The present invention relates to an electrophotographic photoreceptor, and an image forming method, as well as an image forming apparatus, employing said electrophotographic photoreceptor, and a processing cartridge.
BACKGROUND OF THE INVENTION
In recent years, widely employed as electrophotographic photoreceptors, have been organic photoreceptors. Compared to other photoreceptors, organic photoreceptors exhibit advantages in that it is easy to develop materials which correspond to various types of exposure light sources ranging from visible light to infrared rays; it is possible to select materials which result in minimal environmental pollution; their production cost is lower, and the like. However, said organic photoreceptors exhibit disadvantages in that the mechanical strength is insufficient, and when producing numerous prints, the photoreceptor surface tends to be degraded or abraded.
Since electrical and mechanical external force is directly applied to the surface of electrophotographic receptors (hereinafter referred occasionally to as photoreceptors) upon employing charging means, developing means, transfer means, cleaning means, and the like, durability is required to counter such force.
Specifically required is durability to resist wear and abrasion of the photoreceptor surface due to friction, surface degradation due to active oxygen such as ozone, nitrogen oxides, and the like, which are generated during corona charging.
In order to overcome said drawbacks, techniques have been investigated in which a protective layer, exhibiting enhanced strength, is provided on the photoreceptor surface, and the like. For example, Japanese Patent Publication Open to Public Inspection No. 6-118681 discloses that silicone resins are employed as the protective layer of the photoreceptor. However, the transportability of generated carriers results in problems. As a result, particularly at the low humidity environment, which results in an increase in resistance, problems result in response properties. In the field of digital copiers, high image quality has been increasingly demanded, followed by the investigation of the image formation resulting in high resolution. However, the surface protective layer, which exhibits such insufficient response properties, results in diffusion of carriers and it, is impossible to obtain excellent electrostatic latent images.
In order to faithfully reproduce image information as electrostatic latent images, it is required that the electric potential contrast of an exposed area to an unexposed area is sufficiently limited. In order to realize said contrast, it is important to retard the diffusion of carriers from their generated sites to the charge surface. Nihon Gazo Gakkai Shi (Journal of Japan Image Society), Volume 39, No. 3, page 294-295 describes said diffusion as follows: when the ratio of D/&mgr; increases, it is impossible to neglect the effects of the diffusion to an electrostatic latent image, wherein D is the diffusion constant of the charge transport layer, and &mgr; is the drift mobility, while the thickness of the charge transport layer increases, the degradation of latent images increases. However, organic electrophotographic photoreceptors, which are commonly employed, result in a large decrease in the layer thickness due to the sliding of cleaning blades and the like. Accordingly, it has not been preferred to design the thickness of the photosensitive layers, such as a charge transport layer and the like, to be not more than 20 &mgr;m because the durability of the resulting photoreceptor is further degraded.
From the view of the foregoing, investigations have been conducted on electrophotographic receptors which exhibit sufficient strength against the sliding of cleaning blades and the like, and provide sufficient electric potential contrast of the exposed area to an unexposed area in the low humidity environment, a high quality image forming method, and an image forming apparatus employing said electrophotographic photoreceptor, and the like.
SUMMARY OF THE INVENTION
It is an object of the present invention to overcome the aforementioned drawbacks, and to provide a photoreceptor which possesses high surface hardness, high wear resistance, and provides sufficient and consistent electrophotographic properties during repeated use, such as electric potential contrast of an exposed area to an unexposed area at a severe ambience such as high temperature and high humidity as well as low temperature and low humidity, and further, provides an image forming method as well as an image forming apparatus employing said photoreceptor, and a processing cartridge employed in said image forming apparatus.
The inventors of the present invention have conducted investigations to solve the problems described above. As a result, it was discovered that in a photoreceptor in which a hardenable resinous layer having high surface hardness, a decrease in the difference of ionization potential between said hardenable resinous layer and the underlying photosensitive layer, such as, for example, a charge transport layer, effectively retarded the diffusion of carriers of said photoreceptor. Namely, it was discovered that when the difference in ionization potential between said hardenable resinous layer and said transport layer was kept at not more than 0.4 eV and a response time of the total photoreceptor is kept at not more than 0.25 second, electrostatic latent images can be consistently resulting in excellent images.
The present invention and the embodiments thereof will now be described.
1. An electrophotographic photoreceptor comprises an electrically conductive support having thereon a photosensitive layer and a hardenable resinous layer, wherein a difference in ionization potential between said photosensitive layer and said hardenable resinous layer is not more than 0.4 eV, and a response time T
10
defined below is not more than 0.25 second.
<Response Time T
10
>
When a photoreceptor charged at |600 V|±20 V is subjected to a sufficient amount of light irradiation so that |200 V| or less results due to light decay, said response time T
10
refers to the elapsed time during which the average of 10 electrical potentials between surface electric potential data adjacent to each other, which are measured at an interval of 10 milliseconds after light irradiation, reaches 10 V or less.
2. In the electrophotographic photoreceptor of described above, the photosensitive layer preferably comprises a charge generating layer and a charge transport layer, and a difference in ionization potential between said charge transport layer and said hardenable resinous layer is not more than 0.4 eV, and a response time T
10
is not more than 0.25 second.
3. In the electrophotographic photoreceptor of described in 1. or 2. above, said hardenable resinous layer is preferably a siloxane based resinous layer which is obtained by allowing an organic silicon compound having a hydroxyl group or a hydrolyzable group to react with a compound represented by General Formula (1).
B—(R
1
—ZH)
m
General Formula (1)
wherein B represents a univalent or multivalent group comprising structural units having charge transportability, R
1
represents a single bond or divalent alkylene group, Z represents an oxygen atom, a sulfur atom or NH, and m represents an integer of 1 to 4.
4. In the electrophotographic photoreceptor described in 3. above, Z in General Formula (1) is preferably an oxygen atom.
5. In the electrophotographic photoreceptor described in any one of in 1. through 4. above, said hardenable resinous layer is preferably a cross-linking structure containing siloxane based resinous layer exhibiting charge transportability.
6. In the electrophotographic photoreceptor described in 5. above, said siloxane based resinous layer preferably comprises the partial structure represented by the aforementioned General Formula (2).
B—(R
1
—ZH)
m
General Formula (2)
wherein B represents a univalent or mul
Itami Akihiko
Oshiba Takeo
Bierman, Muserlian and Lucas
Goodrow John
Konica Corporation
LandOfFree
Electrophotographic photoreceptor, image forming method,... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Electrophotographic photoreceptor, image forming method,..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Electrophotographic photoreceptor, image forming method,... will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-2996624