Plastic and nonmetallic article shaping or treating: processes – Optical article shaping or treating – Utilizing plasma – electric – electromagnetic – particulate – or...
Reexamination Certificate
2000-01-28
2002-06-11
Vargot, Mathieu D. (Department: 1732)
Plastic and nonmetallic article shaping or treating: processes
Optical article shaping or treating
Utilizing plasma, electric, electromagnetic, particulate, or...
C264S002600
Reexamination Certificate
active
06402995
ABSTRACT:
FIELD OF THE INVENTION
This invention relates to a process for preparing contact lenses and more specifically a novel process for preparing contact lenses made of crosslinked polyvinyl alcohol.
BACKGROUND OF THE INVENTION
Generally, polyvinyl alcohol is obtained by hydrolyzing a polyvinyl ester such as polyvinyl acetate, and it is not easy to crosslink the polyvinyl alcohol.
Up to this time, the crosslinking of polyvinyl alcohol is performed by a way of hydrolyzing polyvinyl acetate to produce polyvinyl alcohol, followed by crosslinking polyvinyl alcohol by using an aldehyde and so on. However, with this method it is not easy to control severely a degree of the crosslinking of polyvinyl alcohol.
Also, a contact lens made of polyvinyl alcohol as a material could not attain to be practical, because it is difficult to shape polyvinyl alcohol into a lens due to its peculiar properties.
On the contrary, Japanese Patent Laid Open No. Hei 40719/1997 discloses a crosslinked polyvinyl alcohol contact lens obtained by processing a copolymer consisting of vinyl acetate and triallyl isocyanurate to form a lenslike copolymer under cooling, followed by hydrolyzing the resultant polymer.
In Japanese Patent Laid Open No. Hei 40719/1997, triallyl isocyanurate as a crosslinking agent and vinyl acetate are bulk-polymerized in a test tube, then the copolymer is subject to machinery processings by grinding and polishing under cooling to form a lens-shaped polymer, followed by hydrolyzing and the lens-shaped polymer obtained is usufull as a crosslinked polyvinyl alcohol contact lens having a high moisture content.
However, it is difficult to handle vinyl acetate having a comparatively small specific gravity and easy vaporization and it is not easy to cotrol a polymerization of the vinyl acetate with triallyl isocyanurate having a comparatively large specific gravity and difficult vaporization due to a thermal polymerization method in a test tube. That is to say, in the case of cutting out several lenses from one piece of a stick-shaped bulky polymer, the lens in a swollen state has a variety of shapes and a shape stability so that there is caused a difficulty of obtaining lenses with equalized quality.
Furthere, since vinyl acetate copolymer of enough hardness could not be obtained at normal temperature, machinery-processings under cooling are required and thus, the preparing steps becomes complicated to maintain the processing conditions and therefore, it is difficult to mass-produce lenses successively at a low cost. Moreover, though the machinery-processings are carried out under cooling, a processing heat arising during the processings has a bad influence on the vinyl acetate copolymer, and as a result the lens surface is roughened and the lens could not be satisfied optically.
Then, the appearance of a process which could be operated easily, for preparing crosslinked polyvinyl alcohol contact lenses having a good shape stability has strongly been desired.
The present invention, meeting the above-mentioned needs, provides a practical and novel process for preparing crosslinked polyvinyl alcohol contact lenses. That is to say, the invention provides a process for preparing crosslinked polyvinyl alcohol contact lenses, which does not roughen the lens surface and can improve a handleability of the lens by improving a shape stability of the completed lens in a swollen state and can mass-produce the lens with equalized quality, as a result of permitting the polymerization can be carried out to a shape of lens without machinery processings.
DISCLOSURE OF THE INVENTION
A process for preparing crosslinked polyvinyl alcohol contact lenses of the present invention comprises preparing a mixture of 100 parts by weight of a vinyl ester expressed by the following structural formula (1)
wherein R is a hydrocarbon group, and 0.05 to 5 parts by weight of triallyl isocyanurate, filling a mold composed of a male mold and a female mold with the mixture, applying ultraviolet ray to form a lens-shaped polymer, and hydrolyzing the resultant polymer.
In the process of the present invention, since the polymerization can be carried out to a shape of lens without machinery processings, the lens surface is not roughened and a shape stability of the completed lens in a swollen state is so excellent that the handleability thereof is good and the lens can be mass-produced with equalized quality.
In this process, since the lens-shaped polymers can be formed at the beginning of the process by the mold in a short time, it is considered that the triallyl isocyanurate can be effectively crosslink the polyvinyl ester for maintaining the shape of the lens.
BEST MODE OF EMBODIMENTS OF THE INVENTION
The present invention will be further described by way of preferable embodiments.
In the present invention, the vinyl ester which becomes a main component of polyvinyl alcohol is expressed by the structural formula (1) and the hydrocarbon group indicated by R is preferably an alkyl group of C
1
to C
8
, an alkenyl group, a cycloalkyl group or an aryl group.
Instances of the alkyl group include methyl group, ethyl group, isopropyl group and hexyl group, instances of the alkenyl group include vinyl group, propenyl group, butenyl group and hexadienyl group, instances of the cycloalkyl group include cyclopentyl group and cyclohexyl group, and instances of the aryl group include phenyl group.
The vinyl ester is preferably vinyl acetate of which R is methyl group, and also vinyl acetate may be used in mixture with other vinyl esters of which R is the alkyl group of C
1
to C
8
, the alkenyl group, the cycloalkyl group, and the aryl group for adjusting a polymerization rate, a monomer viscocity and a hydrolysis rate.
The case in which R is an alkyl group of exceeding C
8
is not preferable because the hydrolysis of the vinyl ester is apt to become difficult and there is a tendency that it is difficult to obtain the polyvinyl alcohol of saponification ratio of 80% or more.
Instances of the vinyl ester may include vinyl acetate, vinyl propionate, vinyl butyrate, vinyl pivalate, vinyl acrylate, vinyl methacrylate and vinyl sorbate.
When a content of triallyl isocyanurate as a crosslink component is less than 0.05 parts by weight, polyvinyl alcohol after the completion of hydrolyzing can not be crosslinked enoughly as a gel and thus, it is difficult to maintain the shape of contact lens. When the content is more than 5 parts by weight, a crosslinking density is so big that flexible contact lens can not be obtained and also the moisture content falls. Therefore, in the present invention, triallyl isocyanurate is used in a range from 0.05 to 5 parts by weight and preferably, from 0.06 to 2 parts by weight.
The molds used in the present invention are molds made of plastic such as polyethylene, polypropylene, polystyrene or ABS resin, or molds made of glass, or these molds in combination with a mold made of metal, which have an optically high precision. Further, since the vinyl ester of which R has a small carbon number such as vinyl acetate is easy to vaporize, it is necessary to pay the greatest care upon air-tightness.
The polymerizing method is a radical polymerization by ultraviolet ray irradiation. In the thermal polymerization method using the mold, when a vinyl ester such as vinyl acetate is vaporized at the beginning of the polymerization, and in the case that the mold has a high air-tightness and an inner pressure of the mold is too high, explosion occurres under certain circumstances. In this point, the polymerization by ultraviolet ray can control easily the polymerization heat compared with the thermal polymerization.
In the present invention, it is also important to control the polymerization reaction by ultraviolet ray in the mold. That is to say, as for the polymerization in the mold and using a small quantity of monomers, it is required to adjust strictly a polymerization reaction rate of the vinyl ester and a polymerization reaction rate of triallyl isocyanurate as the crosslinking agent. The above purpose may be attained by adjusti
Degawa Hiroki
Ikeda Yuki
Uno Kenji
Pitney Hardin Kipp & Szuch LLP
Seed Co., Ltd.
Vargot Mathieu D.
LandOfFree
Process for preparing polyvinyl alcohol contact lenses does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Process for preparing polyvinyl alcohol contact lenses, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Process for preparing polyvinyl alcohol contact lenses will most certainly appreciate the feedback.