Preparation of vinyl aromatic-allylic alcohol copolymers

Synthetic resins or natural rubbers -- part of the class 520 ser – Synthetic resins – Polymers from only ethylenic monomers or processes of...

Reexamination Certificate

Rate now

  [ 0.00 ] – not rated yet Voters 0   Comments 0

Details

C526S086000, C526S087000

Reexamination Certificate

active

06455657

ABSTRACT:

FIELD OF THE INVENTION
The invention relates to the preparation of vinyl aromatic-allylic alcohol copolymers. In particular, the invention relates to the preparation of copolymers having low molecular weights and low hydroxyl functionality.
BACKGROUND OF THE INVENTION
Styrene-allyl alcohol (SM) copolymers are known. U.S. Pat. Nos. 2,588,890 and 2,630,430 teach copolymerzing styrene with allyl alcohol in the presence of oxygen as a catalyst. The SM copolymer thus prepared has high gel content and inferior properties.
U.S. Pat. Nos. 2,894,938 and 2,900,359 teach copolymerizing styrene with allyl alcohol using organic peroxides as initiators in the absence of oxygen. The polymerization is conducted in a bulk process by charging allyl alcohol, styrene and an initiator into a reactor and heating the reaction mixture to a polymerization temperature (180° C. to 300° C.). The SAA copolymer has a low gel content and a functionality greater than 4.
U.S. Pat. No. 2,940,946 teaches a semi-batch process for making SAA copolymers. The process is conducted by initially charging allyl alcohol, an initiator, and a portion of styrene into a reactor, and adding the remaining styrene gradually into the reaction mixture during the polymerization. The copolymer has low color and improved thermal stability.
U.S. Pat. Nos. 5,444,141 and 5,886,114 teach the preparation of SAA copolymers by initially charging allyl alcohol, a portion of styrene and a portion of an initiator into a reactor and gradually adding the remaining styrene and initiator into the reaction mixture during the polymerization. The process gives substantially higher yields compared with the process disclosed in U.S. Pat. No. 2,940,946.
U.S. Pat. No. 6,103,840 teaches an improved process over that of U.S. Pat. No. 5,444,141. The process is conducted by increasing the reaction temperature during the addition of styrene and initiator. The process gives even higher yields of SAA copolymers.
All of the known processes are conducted without the use of a solvent. These processes invariably produce SAA copolymers having hydroxyl functionality (i.e., the number of hydroxyl groups per polymer chain) greater than 4 without using oxygen as a catalyst. When oxygen is used, the copolymers have lower functionality, but they also have high gel content and other inferior properties.
SAA-100 and SAA-101 have been commercially produced for several decades. They have 70/30 and 60/40 molar ratios of recurring units of styrene to allyl alcohol, respectively. Although these SAA copolymers differ in the hydroxyl content or hydroxyl number (OH#, SAA-100: 200 mg KOH/g; SAA-101: 255 mg KOH/g), they have essentially the same hydroxyl functionality (about 5). High hydroxyl functionality of the copolymers gives SAA-based coatings high crosslinking density. However, high functionality also limits the use of the copolymers in many areas, such as in the synthesis of polyester resins where SAA can cause gel formation.
Attempts to reduce the hydroxyl functionality of SAA copolymers have been made. One might try to reduce hydroxyl functionality by reducing the concentration of allyl alcohol during polymerization. This approach fails, however, because the current SAA polymerization process inherently gives higher molecular weight polymers when less allyl alcohol is used. For example, we have recently introduced SAA-103, which has only about 20 mole % of the recurring units of allyl alcohol (hydroxyl number: 125 mg KOH/g). Surprisingly, SAA-103 has even higher hydroxyl functionality (about 7) than SAA-100 or SAA-101. While SAA-103 has a lower concentration of hydroxyl groups, it also has much longer chains, so the number of hydroxyl groups per polymer chain is actually higher than SAA-100 or SAA-101.
A new process for producing SAA copolymers is needed. Ideally, the process would produce SAA copolymers having low hydroxyl functionality and low molecular weights.
SUMMARY OF THE INVENTION
The invention is a process for making copolymers of a vinyl aromatic monomer and an allylic alcohol. The process is performed in the absence of oxygen. The process begins with charging a reactor with an allylic alcohol, 0-50% of the total amount to be used of a vinyl aromatic monomer, 0-100% of the total amount to be used of a free-radical initiator and an organic solvent in an amount greater than or equal to about 10% by weight of the total amount of the vinyl aromatic monomer. The reaction mixture is then heated at a temperature within the range of about 100° C. to about 185° C. The remaining vinyl aromatic monomer and initiator are added to the reaction mixture at a decreasing rate during the polymerization.
DETAILED DESCRIPTION OF THE INVENTION
In the process of the invention, a reactor is initially charged with an allylic alcohol. Allylic alcohols useful in the process preferably have the general structure:
in which R is selected from hydrogen, a C
1
-C
10
alkyl group, or a C
6
-C
10
aryl group. Examples of suitable allylic alcohols are allyl alcohol, methallyl alcohol, and 2-ethyl-2-propen-1-ol. Mixtures of allylic alcohols can be used. Allyl alcohol is preferred because it is commercially available and inexpensive.
The amount of allylic alcohol to be used is determined by many factors. They include the desired hydroxyl number of the copolymer, the reaction temperature, the amount of vinyl aromatic monomer to be used, the amount of initiator to be used, and the manner of the addition of the vinyl aromatic monomer and the initiator. Determining how much allylic alcohol to be used is further complicated by the low reactivity of allylic alcohols. Allylic monomers have much lower reactivity than vinyl aromatic monomers. The great disparity in the monomeric reactivities requires a large excess of allylic alcohols in the reaction mixture to achieve an adequate incorporation of allylic alcohols in the copolymer. In general, more than 25% of excess allylic alcohol is needed. The unreacted allylic alcohol is removed from the polymer after polymerization and is reused.
The reactor is initially charged with 0-50% of the total amount to be used of a vinyl aromatic monomer. Suitable vinyl aromatic monomers preferably have a —CR′═CH
2
group connected to an aromatic group. R′ is hydrogen or a C
1
to C
10
alkyl group. Examples of suitable vinyl aromatic monomers are styrene, &agr;-methylstyrene, &rgr;-methylstyrene, &rgr;-t-butylstyrene, 9-vinylanthracene, 2-vinylnaphthalene, and the like, and mixtures thereof. Styrene is particularly preferred. The total amount of vinyl aromatic monomer to be used is determined mainly by the desired copolymer composition. Vinyl aromatic monomers polymerize essentially completely.
The remaining vinyl aromatic monomer is gradually added, at a decreasing rate, into the reactor during the course of polymerization. At least 50% of the vinyl aromatic monomer is added to the reaction mixture gradually during the polymerization. Preferably, the ratio of the vinyl aromatic monomer to allylic alcohol is kept essentially constant so that the copolymer produced has a relatively uniform composition.
The process comprises initially charging the reactor with 0-100% of the total amount of a free-radical initiator. Suitable free-radical initiators include peroxides, hydroperoxides, peresters, azo compounds, and many others known to the polymer industry. Examples of suitable free-radical initiators are hydrogen peroxide, di-t-butyl peroxide, t-butyl hydroperoxide, cumene hydroperoxide, t-butyl perbenzoate, 2,2′-azobisisobutyronitrile, and the like, and mixtures thereof. The total amount of the initiator to be used is determined by many factors, but mainly by the desired polymerization rate. When more initiator is used, faster polymerization is achieved. Surprisingly, the molecular weight of the copolymer does not vary significantly with the change of the initiator concentration.
It is preferred to add at least 50% of the total amount to be used of the initiator to the reactor gradually during the course of the polymerization. It is also desirable t

LandOfFree

Say what you really think

Search LandOfFree.com for the USA inventors and patents. Rate them and share your experience with other people.

Rating

Preparation of vinyl aromatic-allylic alcohol copolymers does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with Preparation of vinyl aromatic-allylic alcohol copolymers, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Preparation of vinyl aromatic-allylic alcohol copolymers will most certainly appreciate the feedback.

Rate now

     

Profile ID: LFUS-PAI-O-2906171

  Search
All data on this website is collected from public sources. Our data reflects the most accurate information available at the time of publication.