Compositions: ceramic – Ceramic compositions – Clay containing
Reexamination Certificate
2001-03-16
2002-08-27
Marcheschi, Michael (Department: 1755)
Compositions: ceramic
Ceramic compositions
Clay containing
C501S155000, C264S679000, C264S680000, C588S009000, C588S010000, C588S901000, C588S252000
Reexamination Certificate
active
06440884
ABSTRACT:
The present invention utilizes industrial waste and relates to a synergistic composition for producing building bricks and tiles therefrom. It more particularly relates to a process for preparing said composition for providing lighter and stronger bricks and tiles than conventional burnt clay building bricks.
There is a need for new kind of bricks to replace the conventional ones. The conventional burnt clay building bricks are heavier on the foundation and not as strong as the bricks produced by the present invention. The bricks made from the composition of the invention are lighter and have increased compression strength due to the presence of industrial waste.
The disposal of waste is a global problem. Presently, all over the world the industrial waste is disposed off by dumping it down old mine shafts or into other remote landfill sites. But these alternatives do not provide a permanent solution to the problem of disposal of waste. As a result of growing increase in the production of waste due to increase in the number of industries, the scientific community and environmentalists have been concerned about the ecological imbalance degradation caused by such wastes and pollutants.
The present invention addresses itself to the problem and provides a composition which utilizes industrial waste amongst other ingredients for producing bricks and tiles which are lighter and stronger than the conventional bricks.
The industrial waste is derived from the waste generated from electroplating. The disposal of such wastes varies from industry to industry. The industrial wastes from different industries are of different nature. For instance, the waste generated by a power plant is different from that generated by a nuclear plant. The industrial waste employed in the present invention comprises sludge. This sludge may contain hexavalent chromium beyond determination level (BDL), total chromium as chromium in the range of from 145 mg/kg to 1532 mg/kg, copper in the range of from 76.78 to 414 mg/kg and nickel in the range of from 15.72 to 24.62 mg/kg.
Bricks made of fly ash generated by power plants are well known. These bricks can be made of 50% to 80% by weight of fly ash 1% to 5% by weight of alkaline additives and lime. A mix prepared with the foregoing ingredients is subjected to grinding and blending with water. The next step is of moulding the blended mix to obtain a shaped product such as a brick which is cured and aged by conventional methods.
While the prior art composition and process do teach the preparation of a brick composition there is no teaching in respect of a synergistic composition as claimed herein. In the present synergistic composition and process of making it, the ingredients of the composition are clay in an amount of from 60% to 75% by weight of the total composition, sludge in an amount of from 20% to 40% by weight and sand in an amount of 1% to 10% by weight. The especially preferred composition which shows the best results is the one which comprises 65% to 70% of clay, 25% to 30% of sludge and 1% to 5% of sand. Thus the present invention is distinguishable on the basis of the constituents of the composition.
Accordingly, the present invention provides a synergistic composition for making building bricks and tiles comprising a mixture of 60% to 75% by weight of clay, sludge of the kind such as herein described in an amount of from 20% to 40% and 1% to 10% by weight of sand, all percentages being by weight of the total composition.
It will be clear from the foregoing description as well as the description contained hereinafter that a novel brick and tile making composition of the present invention is neither a simple admixture nor a product of a chemical reaction but a synergistic composition having improved and unexpected properties.
A conventional brick and tile composition comprises clay in an amount of 95% of total composition and 5% of sand. These bricks are conventionally of 9″×4.50″×3″ in size and weight between 3 to 3.5 kgs. These are prepared by mixing clay and sand followed by shaping and firing in kilns. The weight of the conventional bricks is greater than the brick made from the composition of the present invention by almost a kilogram. The compressive strength of conventional brick is between 5.5. to 55 Kg/cm
2
and that of the brick produced by the composition of the present invention is above 100 kg/cm
2
. Similarly, water absorption test conducted on a conventional brick as well as the brick made from the invented composition have revealed that the water absorption of the conventional brick was about 10% to 25% and that of the brick prepared by the composition of the present invention was only in the range of from17% to 21%. These and other properties are indeed surprising and unexpected and are different from the properties of the individual ingredients forming the brick composition.
Among other objectives of the present invention is to provide a process for preparing the synergistic composition for making bricks and tiles for construction purposes. It has surprisingly been found that by mixing clay in an mount of from 60% to 75% by weight of the total composition, sludge in an amount of from 20% to 40% by weight of the total composition and sand in an amount of from 1% to 10% by weight, a synergistic composition of inter alia improved compressive strength is produced which can be employed for making bricks and tiles.
Another objective of the present invention is to reduce the land degradation by utilizing the industrial waste from a chemical treatment plant such as an electroplating plant. This is again achieved by employing only 75% of the clay as opposed to 95% in the conventional brick making industry.
The present invention employs the technique of preparing a synergistic composition by mixing clay, industrial waste and sand in a fixed proportion so as to strike a synergistic balance.
By utilizing the industrial waste which comprises at least 20% to 40% of said composition, the requirement of clay from the land has been reduced by at least the same amount. This industrial waste can be in the form of sludge or solid waste obtained from waste water treatment facilities of electro-plating industries. On mixing at least 20% to 40% of industrial waste, 60% to 75% of clay and 1% to 10% of sand by weight of the total composition, the synergistic composition so produced exhibits higher compressive strength and lesser water absorption as seen on comparison of the conventional bricks with the bricks produced by the composition of the present invention. In addition, the brick produced is lighter in weight than the conventional one.
On testing the bricks made from the composition of the present invention it has been found that a compressive strength of above 100 kg/cm
2
to 200 kg/cm2 can be seen. As a result, any construction employing the bricks made from the composition of the present invention will have a higher load bearing capacity than the conventional bricks and therefore the need to provide a deep foundation even for a tall or a medium size structure can be obviated.
Any conventional clay may be used in the preparation of the composition of this invention. However, clays employed can be selected from bentonite, attapulgite and kaolin etc. and their mixture. The particle size of clay can vary from 100 to 200 mesh. It has now been surprisingly found that if clay is replaced by 20% to 40% by weight of industrial waste or sludge not only the degree of compressive strength of brick so produced is improved but also its weight is considerably reduced by at least a kilogram. The conventional brick has a compressive strength of 5.5. kg/cm
2
to 55 kg/cm
2
and the brick prepared from the composition of the present invention has a compressive strength of above 100 kg/cm
2
. The weight of a conventional brick is 3 to 3.5 kgs. whereas the brick prepared by the composition of the present invention has a weight which is about 2 to 2.5 kgs.
The bricks prepared by the novel composition of the present invention were immersed in d
Epstein Robert L.
James Harold
James & Franklin LLP
Marcheschi Michael
LandOfFree
Composition and process for making building bricks and tiles does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Composition and process for making building bricks and tiles, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Composition and process for making building bricks and tiles will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-2893055