Radiation imagery chemistry: process – composition – or product th – Diazo reproduction – process – composition – or product – Composition or product which contains radiation sensitive...
Reexamination Certificate
2001-03-21
2002-05-07
Chu, John S. (Department: 1752)
Radiation imagery chemistry: process, composition, or product th
Diazo reproduction, process, composition, or product
Composition or product which contains radiation sensitive...
C430S165000, C430S192000, C430S193000
Reexamination Certificate
active
06383709
ABSTRACT:
BACKGROUND OF THE INVENTION
The present invention relates to a positive resist composition used in providing resist patterns through irradiation of rays such as ultra violet rays followed by alkaline development and in producing semiconductor integrated circuits and the like.
In a positive resist containing a novolak resin as an alkaline-soluble component and a quinone diazide compound as a radiation-sensitive component, the quinone diazide compound decomposes by irradiation of a ray to produce carboxyl group and turns from alkaline-insoluble to alkaline-soluble innature. This phenomenon is utilized for providing a positive type pattern by irradiation of the ray through a mask (the so-called patterning exposure) followed by alkaline development in an alkaline medium. The above described positive resist containing a novolak/quinone diazide is generally excellent in resolution, and is widely used in the manufacture of integrated circuits.
In recent years, the integrated circuit has become micronized as the degree of integration increases and the formation of submicron patterns is required. As a result, the positive resist with higher resolution and excellent patterning capability (profile) is required. When circuit pattern becomes finer the top surface tends to be rounded or the slant between the top and bottom tends to be conspicuous. As a result, it becomes more difficult to reflect faithfully the mask pattern on the resist pattern to be formed during pattern exposure. Therefore, apositive resist composition is desired which solves those problems and gives a good profile.
The inventors of the present invention have conducted intensive studies to develop a positive resist composition which gives a good profile. As a result, the inventors have found that a positive resist containing an acid generating agent, such as sulfonate of N-hydroxy succinimide, which decomposes to give an acid in an alkaline developer provides an excellent profile, and have disclosed it(JP-A-10-213905, SPIE Vol. 3333, 1280P-1287P, 1998).
After conducting further studies, the inventors have found that a positive resist composition containing a specific composition among sulfonates of N-hydroxy succinimide, namely N-(n-octylsulfonyloxy)succinimide, gives a specifically excellent profile. Thus, the present invention was completed.
SUMMARY OF THE INVENTION
The present invention provides a positive resist composition comprising an alkali-soluble novolak resin, a quinone diazide type radiation-sensitive agent and N-(n-octylsulfonyloxy)succinimide.
DESCRIPTION OF THE PREFERRED EMBODIMENTS
An alkali-soluble novolak resin generally used as an alkaline-soluble component of a known positive resist can also be used as the alkali-soluble novolak resin used in the present invention. The alkali-soluble novolak resin used in the present invention can generally be made by condensing a phenolic compound and an aldehyde in the presence of an acid catalyst. Examples of the phenolic compound include phenol, o-, m- or p-cresol, 2,3-, 2,5-, 3,4- or 3,5-xylenol, 2,3,5-trimethylphenol, 2-, 3- or 4-tert-butyphenol, 2-tert-butyl- 4- or 5-methylphenol, 2-, 4- or 5-methyl resorcinol, 2-, 3- or 4- methoxyphenol, 2,3-, 2,5- or 3,5-dimethoxyphenol, 2-methoxyresorcinol, 4-tert-butyl catechol, 2-, 3- or 4-ethylphenol, 2,5- or 3,5 -diethylphenol, 2,3,5-triethylphenol, 2-naphthol, 1,3-, 1,5- or 1,7-dihydroxylnaphthalene and polyhydroxytriphenyl methane type compounds obtained by condensing xylenol and hydroxybenzaldehyde. These phenolic compounds can be used alone or in combination of two or more.
Examples of the aldehyede include aliphatic aldehyedes such as formaldehyde, acetoaldehyde, propyonaldehyde, n-butylaldehyde, isobutylaldehyde, pivalic aldehyde, n-hexylaldehyde, acrolein- and crotonaldehyde; alicyclic compounds such as cyclohexyaldehyde, cyclopentanaldehyde, furfural and furylacrolein; aromatic aldehydes such as benzaldehyde, o-, m- or p-methylbenzaldehyde, p-ethylbenzaldehyde, 2,4-, 2,5-, 3,4- or 3,5-dimethylbenzaldehyde, o-, m- or p-hydroxybenzaldehyde, o-,m- or p-anisic aldehyde and vanillin; and aromoaliphic aldehydes such as phenyl acetaldehyde, and cinnamic aldehyde. These aldehydes can also be used alone or in combination of two or more. Among them, formaldehyde is preferable because it is readily available in the industry.
Examples of the acid catalysts usable in condensing the phenolic compound and aldehyde include inorganic acids such as hydrochloric acid, sulfuric acid, perchloric acid andphosphoric acid; organic acids such as formic acid, acetic acid, oxalic acid, trichloroacetic acid and p-toluenesulfonic acid; bivalent metallic salts such as zinc acetate, zinc chloride and magnesium acetate. Those acid catalysts can be used alone or in combination of two or more. The condensation reaction can be carried out in a usual way, for example, for 2 to 30 hours at 60 to 120° C.
A novolak resin obtained by the condensation is preferably subjected to a fractionation to increase high molecular weight component. It is preferable that, when expressed in a gel permeation chromatography (GPC) pattern, the pattern area of the components with a molecular weight not higher than 1000 is not higher than 25%, more preferably not higher than 20%, based on the total pattern area except for the unreacted phenolic compounds. Here, the GPC pattern is measured using a 254 nm UV detector, and the molecular weight is in terms of the molecular weight of polystyrene.
It is useful to add a low molecular weight alkali-soluble phenol compound, for example the one with a molecular weight of not higher than 1,000, to the novolak resin in which the high molecular weight component was increased. Such alkali-soluble low molecular weight phenol compounds have preferably at least two phenolic hydroxyl groups as disclosed in JP-A-2-275955 (U.S. Pat. Nos. 5,456,995 and 5,456,996) and JP-A-2-2560. In case an alkali-soluble phenol compound with a molecular weight of not higher than 1,000 is used, it is desirable that the compound is present in 3 to 40 percent by weight based on the total amount of the novolak resin and the alkali-soluble phenol compound.
A quinone diazo-type radiation-sensitive agent generally used in the positive resist field can be used as the quinone diazo-type radiation-sensitive agent used in the present invention. Generally, an o-quinone diazosulfonic acid ester of a compound having one or more phenolic hydroxyl groups can be used. Preferable are 1,2-naphthoquinonediazo-5- or 4-sulfonic acid ester or 1,2-benzoquinone diazo-4-sulfonic acid ester of polyhydroxy compounds having at least three phenol hydroxyl groups. Such esters can be made by reacting the compounds having the aforesaid hydroxyl groups with o-quinone diazosulfonic acid halide in the presence of a base such as triethyl amine. Among O-quinone diazosulfonic acid halides, 1,2-naphthoquinone diazo-5-sulfonic acid chloride is especially preferable. Such quinone diazo-type radiation-sensitive agents can be used alone as combination of one or two agents. It is preferable that the radiation-sensitive agent is present in 10 to 100 percent by weight, more preferably 10 to 50 percent by weight based on the total amount of the novolak resin and the aforesaid low molecular weight alkali-soluble phenol compound used as necessary.
The positive resist composition of the present invention comprises N-(n-octylsulfonyloxy)succinimide in addition to the alkali-soluble novolak resin and the quinone diazo-type radiation-sensitive agent mentioned above. This compound can be prepared by condensation of N-hydroxy succinimide with n-octylsulfonyl chloride under basic medium.
The content of N-(n-octylsulfonyloxy)succinimide is generally 0.01 to 25 percent by weight, preferably 0.1 to 10 percent by weight based on the total solid content in the composition.
The positive resist composition of the present invention is generally applied as a resist solution on a substrate such as silicon wafer. That is, the above-mentioned respective components are dissolved in a solvent to prepare a resist solution and
Lee Sang-Ho
Tomioka Jun
Uetani Yasunori
Birch & Stewart Kolasch & Birch, LLP
Chu John S.
Sumitomo Chemical Company Limited
LandOfFree
Positive resist composition comprising... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Positive resist composition comprising..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Positive resist composition comprising... will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-2851146