ABSTRACT:
BACKGROUND OF THE INVENTION
1. Field of the Invention
The present invention relates to a thread-wound golf ball which has increased resilience, increased travel distance, and provides a favorable feel when hit.
2. Description of the Related Art
A thread-wound golf ball is manufactured in such a manner that rubber thread is wound around a center ball to form a thread layer, and a cover is formed to surround the thread layer. To increase the resilience of a thread-wound golf ball to thereby increase its travel distance, a technique for increasing the extendibility of rubber thread has conventionally been employed. This technique crystallizes rubber thread to a sufficient degree through extension (hereinafter this process is referred to as “extension crystallization”), thereby preventing further crystallization of the rubber thread which would otherwise occur when the ball deforms upon impact.
However, the technique for increasing the extendibility of rubber thread has the following drawback. Since the hardness of a thread-wound golf ball increases with the degree of extension crystallization of rubber thread, the degree of backspin becomes greater than that of a solid golf ball when the extendibility of the rubber thread exceeds a predetermined level. Thus, the travel distance of the thread-wound golf ball becomes shorter than that of the solid golf ball.
In view of the foregoing, the present inventors have carried out studies on the relationship between resilience of a thread-wound golf ball and the material of thread used in the thread layer thereof. The following four patent publications disclose conventional golf balls, each utilizing thread other than rubber thread to form a thread layer.
(1) JP Patent Laid-Open Publication No. 57(1982)-160479
In the golf ball disclosed in this publication, filament-like elastic fibers having an initial elastic modulus of at least 5 g/de and an elastic recovery ratio (50% extension) of at least 70% are used as thread for forming a thread layer. The filament-like elastic fibers are formed of polyolefine, polyacetal, polyamide, crystalline polypropylene, or polyoxymethylene.
(2) JP Patent Laid-Open Publication No. 57(1982)-170272
This publication discloses two types of thread-wound golf balls. In the first golf ball, filament-like elastic fibers formed of a thermoplastic polymer are used as thread for forming a thread layer. The cross-sectional area of each filament changes along the longitudinal direction at random intervals, and the intra-filament cross-sectional-area variation coefficient with respect to the longitudinal direction falls within a range of 0.05 to 1.0. The fibers have an initial elastic modulus of at least 5 g/de and an elastic recovery ratio (50% extension) of at least 70%.
In the second golf ball, a bundle consisting of a large number of filaments formed of a thermoplastic polymer is used as thread for forming a thread layer. The filament bundle has the following features. (1) In each filament constituting the bundle, the cross-sectional area changes along the longitudinal direction at random intervals. (2) The intra-filament cross-sectional-area variation coefficient with respect to the longitudinal direction falls within a range of 0.05 to 1.0. (3) The fibers have an initial elastic modulus of at least 5 g/de and an elastic recovery ratio (50% extension) of at least 70%. (4) The variation in cross-sectional area of filaments, as measured along an arbitrary plane perpendicular to the filament axis and expressed by use of an intra-bundle filament cross-sectional-area variation coefficient, falls within a range of 0.05 to 1.5.
(3) JP Patent Laid-Open Publication No. 10(1998)-247
This publication discloses a golf ball in which a thin wire formed of a shape memory alloy is used as thread for forming a thread layer.
(4) British Patent No. 620208
This patent discloses a golf ball in which a resin thread is used as thread for forming a thread layer. The resin thread has a property such that the resin is not oriented in an ordinary state, but is oriented when deformed. The resin thread is formed of vinylidene chloride or nylon.
The techniques employed in the golf balls disclosed in the above-described four patent publications are not necessarily satisfactory in terms of increasing resilience to thereby increase travel distance.
SUMMARY OF THE INVENTION
In view of the foregoing, an object of the present invention is to provide a thread-wound golf ball which has increased resilience, has increased travel distance, and provides a favorable feel when hit.
The present inventors found that the following advantageous effects are provided when rubber thread and resin thread are mixedly wound around a center ball, especially when the resin thread formed of a resin (such as polyester resin or polyurethane resin) which has relatively high resilience and is softer than rubber thread undergone extension crystallization is wound around the center ball together with the rubber thread.
(1) Resilience can be secured by means of sufficient extension of the rubber thread. In addition, since soft resin thread is co-present with the rubber thread, the golf ball does not lose softness. Therefore, the degree of backspin can be decreased, while high resilience is maintained, so that the golf ball provides a travel distance comparable to that of a solid golf ball.
(2) Since resin thread is co-present with rubber thread, the golf ball can provide softer hit-feel as compared with conventional thread-wound golf balls.
The present invention was accomplished on the basis of the above-described findings, and provides a thread-wound golf ball comprising a center ball, a thread layer, and a cover, wherein the thread layer is formed of rubber thread and resin thread mixedly wound around the center ball.
DESCRIPTION OF THE PREFERRED EMBODIMENT
The present invention will now be described in more detail. No limitation is imposed on the type of the center ball employed in the thread-wound golf ball of the present invention; the center ball may be a solid center ball obtained through molding a synthetic rubber into a spherical shape, or a liquid center ball formed of a spherical rubber bag filled with liquid. The center ball typically has an outer diameter of 26 to 36 mm. If necessary, the center ball may be formed to have a plurality of layers. When a solid center ball is employed, deformation of the solid center ball upon application of a load of 100 kg is preferably 3.5 to 10.0 mm.
The material of the resin thread preferably has a Shore D hardness of 15 to 50, more preferably 20 to 45, in order to yield a thread-wound golf ball providing a soft feel when hit.
The rubber thread preferably has a width of 1.0 to 2.5 mm and a thickness of 0.3 to 0.6 mm before winding. When the width is less than 1.0 mm or the thickness is less than 0.3, the strength of the rubber thread is insufficient, with the result that the rubber thread may frequently break upon winding. Thus, workability and quality may deteriorate. When the width is greater than 2.5 mm or the thickness is greater than 0.6, the sphericity of a spherical body obtained as a result of winding rubber thread and resin thread on the center ball is insufficient, so that the thickness of the cover becomes nonuniform, with the result that resilience lowers depending on the position of the golf ball at which the golf ball is hit.
The extendibility of the rubber thread upon winding is preferably set to a range of 700 to 1000%, more preferably 750 to 900%, in order to increase resilience of the golf ball to thereby increase travel distance.
The resin thread is preferably formed of a resin which has relatively high resilience and is softer than rubber thread undergone extension crystallization. Examples of the resin thread include, but are not limited to, resin thread containing polyester resin or polyurethane resin as a main component; specifically, resin thread containing, as a main component, polyester thermoplastic elastomer or polyurethane elastomer. More specific examples include Hytrel 3078, 4047, and 4767 (Shore D ha
Maruko Takashi
Nakamura Atsushi
Yamagishi Hisashi
Bridgestone Sports Co. Ltd.
Hunter, Jr. Alvin A.
Sewell Paul T.
LandOfFree
Thread-wound golf ball does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Thread-wound golf ball, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Thread-wound golf ball will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-2825225