Multilayer conductive polymer positive temperature...

Metal working – Method of mechanical manufacture – Electrical device making

Reexamination Certificate

Rate now

  [ 0.00 ] – not rated yet Voters 0   Comments 0

Details

C338S0220SD, C338S312000, C338S313000, C338S203000, C029S610100, C029S612000

Reexamination Certificate

active

06223423

ABSTRACT:

FEDERALLY SPONSORED RESEARCH OR DEVELOPMENT
Not Applicable
BACKGROUND OF THE INVENTION
The present invention relates generally to the field of conductive polymer positive temperature coefficient (PTC) devices. More specifically, it relates to conductive polymer PTC devices that are of laminar construction, with more than a single layer of conductive polymer PTC material, and that are especially configured for surfacemount installations.
Electronic devices that include an element made from a conductive polymer have become increasingly popular, being used in a variety of applications. They have achieved widespread usage, for example, in overcurrent protection and self-regulating heater applications, in which a polymeric material having a positive temperature coefficient of resistance is employed. Examples of positive temperature coefficient (PTC) polymeric materials, and of devices incorporating such materials, are disclosed in the following U.S. Pat. Nos.:
3,823,217—Kampe
4,237,441—van Konynenburg
4,238,812—Middleman et al.
4,317,027—Middleman et al.
4,329,726—Middleman et al.
4,413,301—Middleman et al.
4,426,633—Taylor
4,445,026—Walker
4,481,498—McTavish et al.
4,545,926—Fouts, Jr. et al.
4,639,818—Cherian
4,647,894—Ratell
4,647,896—Ratell
4,685,025—Carlomagno
4,774,024—Deep et al.
4,689,475—Kleiner et al.
4,732,701—Nishii et al.
4,769,901—Nagahori
4,787,135—Nagahori
4,800,253—Kleiner et al.
4,849,133—Yoshida et al.
4,876,439—Nagahori
4,884,163—Deep et al.
4,907,340—Fang et al.
4,951,382—Jacobs et al.
4,951,384—Jacobs et al.
4,955,267—Jacobs et al.
4,980,541—Shafe et al.
5,049,850—Evans
5,140,297—Jacobs et al.
5,171,774—Ueno et al.
5,174,924—Yamada et al.
5,178,797—Evans
5,181,006—Shafe et al.
5,190,697—Ohkita et al.
5,195,013—Jacobs et al.
5,227,946—Jacobs et al.
5,241,741—Sugaya
5,250,228—Baigrie et al.
5,280,263—Sugaya
5,358,793—Hanada et al.
One common type of construction for conductive polymer PTC devices is that which may be described as a laminated structure. Laminated conductive polymer PTC devices typically comprise a single layer of conductive polymer material sandwiched between a pair of metallic electrodes, the latter preferably being a highly-conductive, thin metal foil. See, for example, U.S. Pat. Nos. 4,426,633—Taylor; 5,089,801—Chan et al.; 4,937,551—Plasko; and 4,787,135—Nagahori; and International Publication No. WO97/06660.
A relatively recent development in this technology is the multilayer laminated device, in which two or more layers of conductive polymer material are separated by alternating metallic electrode layers (typically metal foil), with the outermost layers likewise being metal electrodes. The result is a device comprising two or more parallel-connected conductive polymer PTC devices in a single package. The advantages of this multilayer construction are reduced surface area (“footprint”) taken by the device on a circuit board, and a higher current-carrying capacity, as compared with single layer devices.
In meeting a demand for higher component density on circuit boards, the trend in the industry has been toward increasing use of surface mount components as a space-saving measure. Surface mount conductive polymer PTC devices heretofore available have been generally limited to hold currents below about 2.5 amps for packages with a board footprint that generally measures about 9.5 mm by about 6.7 mm. Recently, devices with a footprint of about 4.7 mm by about 3.4 mm, with a hold current of about 1.1 amps, have become available. Still, this footprint is considered relatively large by current surface mount technology (SMT) standards.
The major limiting factors in the design of very small SMT conductive polymer PTC devices are the limited surface area and the lower limits on the resistivity that can be achieved by loading the polymer material with a conductive filler (typically carbon black). The fabrication of useful devices with a volume resistivity of less than about 0.2 ohm-cm has not been practical. First, there are difficulties inherent in the fabrication process when dealing with such low volume resistivities. Second, devices with such a low volume resistivity do not exhibit a large PTC effect, and thus are not very useful as circuit protection devices.
The steady state heat transfer equation for a conductive polymer PTC device may be given as:
0=[I
2
R(f(T
d
))]−[U(T
d
−T
a
)],  (1)
where I is the steady state current passing through the device; R(f(T
d
)) is the resistance of the device, as a function of its temperature and its characteristic “resistance/temperature function” or “R/T curve”; U is the effective heat transfer coefficient of the device; T
d
is temperature of the device; and T
a
is the ambient temperature.
The “hold current” for such a device may be defined as the value of I necessary to trip the device from a low resistance state to a high resistance state. For a given device, where U is fixed, the only way to increase the hold current is to reduce the value of R.
The governing equation for the resistance of any resistive device can be stated as
R=&rgr;L/A,  (2)
where &rgr; is the volume resistivity of the resistive material in ohm-cm, L is the current flow path length through the device in cm, and A is the effective cross-sectional area of the current path in cm
2
.
Thus, the value of R can be reduced either by reducing the volume resistivity &rgr;, or by increasing the cross-sectional area A of the device.
The value of the volume resistivity p can be decreased by increasing the proportion of the conductive filler loaded into the polymer. The practical limitations of doing this, however, are noted above.
A more practical approach to reducing the resistance value R is to increase the cross-sectional area A of the device. Besides being relatively easy to implement (from both a process standpoint and from the standpoint of producing a device with useful PTC characteristics), this method has an additional benefit: In general, as the area of the device increases, the value of the heat transfer coefficient also increases, thereby further increasing the value of the hold current.
In SMT applications, however, it is necessary to minimize the effective surface area or footprint of the device. This puts a severe constraint on the effective cross-sectional area of the PTC element in device. Thus, for a device of any given footprint, there is an inherent limitation in the maximum hold current value that can be achieved. Viewed another way, decreasing the footprint can be practically achieved only by reducing the hold current value.
There has thus been a long-felt, but as yet unmet, need for very small footprint SMT conductive polymer PTC devices that achieve relatively high hold currents.
SUMMARY OF THE INVENTION
Broadly, the present invention is a conductive polymer PTC device that has a relatively high hold current while maintaining a very small circuit board footprint. This result is achieved by a multilayer construction that provides an increased effective cross-sectional area A of the current flow path for a given circuit board footprint. In effect, the multilayer construction of the invention provides, in a single, smallfootprint surface mount package, two or more PTC devices electrically connected in parallel.
In one aspect, the present invention is a conductive polymer PTC device comprising, in a preferred embodiment, five alternating layers of metal foil and PTC conductive polymer, with electrically conductive interconnections to form two conductive polymer PTC devices connected to each other in parallel, and with termination elements configured for surface mount termination.
Specifically, two of the foil layers form, respectively, upper and lower electrodes, while the third foil layer forms a center electrode. A first conductive polymer layer is located between the upper and center electrodes, and a second conductive polymer layer is located between the center and lower electrodes. Each of the upper and lower electrodes is separated into an isolated portion a

LandOfFree

Say what you really think

Search LandOfFree.com for the USA inventors and patents. Rate them and share your experience with other people.

Rating

Multilayer conductive polymer positive temperature... does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with Multilayer conductive polymer positive temperature..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Multilayer conductive polymer positive temperature... will most certainly appreciate the feedback.

Rate now

     

Profile ID: LFUS-PAI-O-2540893

  Search
All data on this website is collected from public sources. Our data reflects the most accurate information available at the time of publication.