Chemistry: electrical current producing apparatus – product – and – Current producing cell – elements – subcombinations and... – Plural cells
Reexamination Certificate
1999-05-12
2001-08-21
Kalafut, Stephen (Department: 1745)
Chemistry: electrical current producing apparatus, product, and
Current producing cell, elements, subcombinations and...
Plural cells
C429S123000, C429S141000, C429S142000
Reexamination Certificate
active
06277515
ABSTRACT:
BACKGROUND OF THE INVENTION
1. Field of the Invention
The present invention relates to a solid electrolyte battery having excellent heavy load resistance, pulse discharge load resistance and over discharge resistance.
2. Description of the Related Art
Since a variety of electronic apparatuses have dramatically progressed, research and development of secondary battery have been carried out. The reason for this lies in that the secondary battery can continuously be used for a long time and the same can again be charged to serve as an economical power source. The representative secondary batteries are exemplified by a non-aqueous electrolyte secondary battery, such as a lithium ion battery, and an all-solid electrolyte polymer battery. The all-solid electrolyte polymer battery incorporates all-solid polymer electrolyte containing a cation conductive materials, such as polyether oxide, polyester, polyimide, crosslinked polyether or polyether derivatives.
In particularly, the all-solid electrolyte polymer battery incorporates a heating-permissible electrolyte. Since the foregoing electrolyte is embedded in high polymer chains of the polymers, frame resistance and a self-extinguishing characteristic can be imparted. As compared with the non-aqueous electrolyte secondary battery, the all-solid electrolyte polymer battery has significant safety characteristics to resist disturbance, such as an external shock, unintentional overcharge and unintentional leaving in a hot atmosphere. As described above, the all-solid electrolyte polymer battery has satisfactory safety.
The all-solid electrolyte polymer battery suffers from a problem in that a poor ion conductivity &sgr; of 10
−4
S (siemens)/cm to 10
−5
S/cm in the vicinity of room temperature. As described above, the polymer battery incorporates the all-solid electrolyte polymer battery having superior safety to that of the non-aqueous electrolyte secondary battery. Moreover, the polymer battery contains the electrolyte which is the non-aqueous electrolyte having the poor ion conductivity embedded in the polymers. Therefore, there arises a problem in that an output of an electric current which can be obtained per unit hour is excessively small as compared with that of the non-aqueous electrolyte secondary battery. As a result, there arises a problem in that use of the all-solid electrolyte polymer battery is limited.
Therefore, a polymer battery having an ion conductivity of 10
−3
S/cm or greater which is a practical value from the viewpoint of industrial use has been obtained and investigated. Note that all-solid electrolytes have been reported which exhibit a high ion conductivity of 10
−3
S/cm at high temperatures in the vicinity of 100° C. which is a level required from the viewpoint of practical use. However, the above-mentioned high temperature condition is not a condition under which the battery is frequently used from a viewpoint of the practical use. Therefore, simplicity and the shape of the polymer battery are limited in the field of use of the polymer battery.
An attempt to improve the ion conductivity of the all-solid electrolyte polymer battery has been made by raising the concentration of salt in the polymer electrolyte. However, the above-mentioned method cannot improve the ion conductivity. The reason for this lies in that rise in the concentration of salt in the polymer electrolyte enhances crystallization of the polymers. As a result, the ratio of ions which can freely be moved in the polymer electrolyte cannot be raised.
Another method has been investigated in which the concentration of salt in the polymer electrolyte is raised and a crystallization inhibitor, such as isocyanate, is mixed with the polymer. The above-mentioned method, however, causes isocyanate to react with cation. What is worse, introduction of active protons results in the severer conditions being required. Therefore, the foregoing method is not an effective method.
Another method has been investigated which improves the ion conductivity of the all-solid electrolyte polymer battery. The method uses molten salt to raise the density of carriers. Although lithium double salt has solubility, the double salt can easily be exploded. Therefore, safety cannot easily be realized.
Another means has been disclosed in which side-chain molecular structures provided for main chains of the polymers have the ion conductivity in place of the main chains of the molecular structures arranged in the polymers to form a mesh configuration. If the foregoing method is employed, a required ion conductivity cannot be obtained. However, a poor ion conductivity at room temperature is realized which is about 10
−4
S/cm which is lower than a practical value by one digit.
As a practical means for achieving an ion conductivity &sgr; of 10
−3
S/cm, a composite electrolyte has been disclosed which has the ion conductivity by impregnating a porous film made of polypropylene or polyvinylidene fluoride with organic solvent, such as polycarbonate, ethylene carbonate or &ggr;-butyllactone. As a matter of course, the foregoing porous film, however, has unsatisfactory mechanical strength. As a result, short circuit easily occurs when external force is exerted. In particular, the polymer electrolyte cannot resist dendrite short circuit, causing the organic solvent with which the porous film has been impregnated to easily be exudated. Therefore, a battery manufactured by the above-mentioned method cannot be included in the category of the polymer electrolyte battery.
As another composite electrolyte, a method has been disclosed which uses a high polymer gel film in which non-proton organic solvent is confined in small spaces in a 3D network structure of crosslinked high polymer molecules.
The electrolyte containing the high polymer gel film has required mechanical strength as compared with that of the all-solid electrolyte. Moreover, an ion conductivity of an order of 10
−3
S/cm can be obtained. Therefore, the foregoing method is considered to be a most practical solving means.
As compared with the conventional non-aqueous electrolyte secondary battery, such as the lithium ion battery, the polymer battery incorporating the high polymer gel film does not require a pressure-resisting container because organic solvent is confined in the gel form polymer. Moreover, a weight energy density and a volume energy density can be obtained which are realized when the foregoing battery has been formed into a battery pack and which are similar to or superior to those of the conventional non-aqueous electrolyte secondary battery. The polymer battery incorporating, the high polymer gel film is able to maintain the shape thereof with thin structures of electrodes. Therefore, the foregoing polymer battery has a possibility that a very thin battery cell can be manufactured. Therefore, there has been expected to apply the foregoing polymer batteries to notebook personal computers and very-thin portable apparatuses. Similar to the all-solid electrolyte polymer battery, the polymer battery incorporating the high polymer gel film contains the high polymer chains of the polymers which are impregnated with the electrolyte. Therefore, frame resistance and a self-extinguishing characteristic can be imparted, causing, satisfactory safety to be realized.
As described above, the polymer battery incorporating, the high polymer gel film has the ion conductivity of the electrolyte, which is 10
−3
S/cm, similar to that of the electrolyte of the non-aqueous electrolyte secondary battery. However, the foregoing polymer battery suffers from low reaction speed in the interface between the electrolyte and the active materials as compared with the non-aqueous electrolyte secondary battery. Therefore, an output of electric currents which can be obtained per unit hour is inferior to that of the non-aqueous electrolyte secondary battery.
As compared with other secondary batteries including a Ni—Cd secondary battery and a Ni—MH secondary battery, the all-solid electrolyte polymer
Kalafut Stephen
Ruthkosky Mark
Sonnenschein Nath & Rosenthal
Sony Corporation
LandOfFree
Solid electrolyte battery with charge accumulating portions... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Solid electrolyte battery with charge accumulating portions..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Solid electrolyte battery with charge accumulating portions... will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-2471113