ABSTRACT:
Magnetically actuated devices such as, e.g., switches and synchronizers typically comprise a magnetically semihard component having a square B-H hysteresis loop and high remanent induction. Among alloys having such properties are Co-Fe-V, Co-Fe-Nb, and Co-Fe-Ni-Al-Ti alloys which, however, contain undesirably large amounts of cobalt.
According to the invention, devices are equipped with a magnetically semihard, high-remanence Fe-Mo-Ni alloy which comprises Mo in a preferred amount in the range of 2-26 weight percent and Ni in a preferred amount in the range of 0.5-15 weight percent.
Magnets made from alloys of the invention may be shaped, e.g., by cold drawing, rolling, bending, or flattening and may be used in devices such as, e.g., electrical contact switches, hysteresis motors, and other magnetically actuated devices.
Preparation of alloys of the invention may be by a treatment of annealing and aging or deformation and aging.
REFERENCES:
patent: 2707680 (1955-05-01), Succop
patent: 3624568 (1971-11-01), Olsen et al.
patent: 3805378 (1974-04-01), Archer et al.
patent: 3971676 (1976-07-01), Detert et al.
patent: 4128420 (1978-12-01), Esper et al.
patent: 4162157 (1979-07-01), Parker et al.
patent: 4340435 (1982-07-01), Jin et al.
L. R. Moskowitz, Permanent Magnet Design and Application Handbook, Cahners Books, 1976, pp. 211-220.
M. R. Pinnel, "Magnetic Materials for Dry Reed Contacts", IEEE Transactions on Magnetics, vol. MAG-12, 1976, pp. 789-794.
R. M. Bozorth, Ferromagnetism, Van Nostrand, 1959, pp. 34-37, 236-239, 416-417.
W. S. Messkin et al., "Experimentelle Nachprufung der Akulovschen Theorie der Koerzitivkraft", Zeitschrift fur Physik, vol. 98, 1936, pp. 610-623.
H. Masumoto, "Characteristics of Fe-Mo and Fe-W Semihard Magnet Alloys", Journal of the Japanese Institute of Metals, vol. 43, 1979, pp. 506-512.
K. S. Seljesater et al., "Magnetic and Mechanical Hardness of Dispersion Hardened Iron Alloys", Transactions of the American Society for Steel Treating, vol. 19, pp. 553-576.
W. Koster, "Das System Eisen-Nickel-Molybdan", Archiv fur das Eisenhuttenwesen, vol. 8, (1934), pp. 169-171.
Metals Handbook, 8th Ed., vol. 8, American Society for Metals, 1973, p. 431.
Jin Sung-ho
Tiefel Thomas H.
Bell Telephone Laboratories Incorporated
Businger Peter A.
Sheehan John P.
LandOfFree
Method for making a high remanence Fe-Mo-Ni magnetic element does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Method for making a high remanence Fe-Mo-Ni magnetic element, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Method for making a high remanence Fe-Mo-Ni magnetic element will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-158086